Abstract:Under extreme conditions such as high speed and heavy load, 18Cr2Ni4WA steel cannot meet the service requirements even after carburizing and quenching processes. In order to obtain better surface mechanical properties and tribological property, a hollow cathode ion source diffusion strengthening device was used to nitride the traditional carburizing and quenching samples. Unlike traditional ion carbonitriding technology, the low-temperature ion carbonitriding technology used in this article can increase the surface hardness of the material by 50% after 3 h of treatment, from the original 600 HV0.1 to 900 HV0.1, while the core hardness only decreases by less than 20%. The effect of post-ion carbonitriding treatment on mechanical properties and tribological properties of the carburized and quenched 18Cr2Ni4WA steel was investigated. Samples in different treatment are characterized using optical microscopy (OM), scanning electron microscopy (SEM), optimal SRV-4 high temperature tribotester, as well as Vickers hardness tester. Under two conditions of 6N light load and 60 N heavy load, compared with untreated samples, the wear rate of ion carbonitriding samples decreased by more than 99%, while the friction coefficient remained basically unchanged. Furthermore, the careful selection of ion nitrocarburizing and carburizing tempering temperatures in this study has been shown to significantly enhance surface hardness and wear resistance, while preserving the overall hardness of the carburized sample. The present study demonstrates the potential of ion carbonitriding technology as a viable post-treatment method for carburized gears.

Study on Low Temperature Liquid Nitrocarburizing

Experiments and numerical simulation of dynamic cool-down process of stainless steel plate in liquid nitrogen bath

Effect of N on the Precipitation Behaviours of the Reduced Activation Ferritic/martensitic Steel CLF-1 after Thermal Ageing

Study on Low Temperature Gas Multielement Co-penetration on Alloy Carburizing Steel Surface

Effects of Initial Microstructure on the Low-Temperature Plasma Nitriding of Ferritic Stainless Steel

The thermal process for hardening the nitrocarburized layers of a low-carbon steel

Effect of Post-Plasma Nitrocarburized Treatment on Mechanical Properties of Carburized and Quenched 18Cr2Ni4WA Steel

Surface Roughness and Morphology of Gas Nitrocarburized Layer for Steel-Plate

Surface properties of low alloy steel treated by plasma nitrocarburizing prior to laser quenching process

New Process of Drop Feed Gas Carburizing with High Rate

Advances in Low-Temperature Nitriding and Carburizing of Stainless Steels and Metallic Materials: Formation and Properties

Short time nitriding and nitrocarburizing of martensitic stainless steel

Research Progress of Gas Soft-nitriding Technology

Structural and Tribological Properties of Sulfonitrocarburizing Layers Prepared by Plasma Nitrocarburizing and Low Temperature Ion Sulfurizing

Low Temperature Nitriding of Metal Alloys for Surface Mechanical Performance

Study of M50NiL steel under carburizing and nitriding duplex treatment

Experimental Study on Vacuum Carburizing Process for Low-Carbon Alloy Steel

Optimizing the mechanical properties of M50NiL steel by plasma nitrocarburizing

Mechanical properties of low-temperature gaseous carburizated layer in 316L stainless steel based on nano-indentation and four-point bending tests

Low-Temperature Carburization of Austenitic Stainless Steels

Gradient microstructure evolution and hardening mechanism of carburized steel under novel heat treatment