Abstract:We analyzed the factors affecting the gas carburizing microstructure of parts for constant velocity joints. Gas carburizing 0.15-0.20C1.13-1.14Cr chromium alloy steel used in automobile drive units is characterized by changing the properties of the carburizing layer in the depth direction. The experimental conditions were set to enable field application. The components of the specimen to be used for gas carburization were analyzed by X-ray fluorescence. Changes in the mechanical properties of the carburized layer were analyzed by micro-hardness, microstructure, and carburizing content. The gas carburization cycle was selected based on the simulation results. The characteristics change before and after carburization of two samples with different carbon and chromium content were analyzed. The carburization temperature that can be used for manufacturing automobile parts was 930°C, the carbon potential required for carburization was 0.90wt%, and the carbon potential required for diffusion was 0.75wt%. The inner and outer hardness values of the carburized layer satisfying the effective hardening depth of 550Hv were 400Hv-740Hv. In the case of 0.20C alloy steel, the effective hardening depth with a carburizing amount of 0.36wt% and a hardness of 550Hv was 1.467 mm. also in the case of 0.15C steel, its effective hardening depth was 0.746 mm. The simulation results for selecting the carburizing heat treatment conditions and the carbon change in the carburizing layer showed a similar trend. The carburizing structure related to hardness change was martensite. As a result of EPMA, SEM, and XRD analysis, the amount of carburized and the amount of martensite structure correlated, and the martensite increased as the amount of carburized increasing. As a result of EPMA analysis, the smaller the carburizing content the greater the depth of carburization. We intend to proceed with optimization conditions for mass production in connection with wear resistance and fatigue. It is expected that these results will contribute to the improvement of durability of automobile driving parts.

Study on Low Temperature Gas Multielement Co-penetration on Alloy Carburizing Steel Surface

Experimental Study on Vacuum Carburizing Process for Low-Carbon Alloy Steel

Effect of Carbon Concentration Gradient on Multi-Level Composite Microstructure and Performance of M50NiL Steel

Experimental Study and Computer Simulation on Multicomponent Diffusion in Multiphase Dispersions During Solid Carburizing of HP40Nb and KHR45A Alloys

Gradient microstructure evolution and hardening mechanism of carburized steel under novel heat treatment

Microstructures and Mechanical Properties of Surface and Center of Carburizing 23cr2ni2si1mo Steel Subjected to Low-Temperature Austempering

Influences of Partial Substitution of C by N on the Microstructure and Mechanical Properties of 9cr18mo Martensitic Stainless Steel

Preparation and microstructural characterization of hard bainite in surface layer of low-carbon alloy steel

Preparation and Microstructure of Hard Bainite in Surface Layer of Carburized 20crmnmoal Steel

Carburization-induced microstructure evolution and hardening mechanism of 18CrNiMo7-6 steel

Factors Affecting the Hardness Characteristics of Microstructures in Gas Carburized Chromium Alloy Steels

Microstructure and mechanical properties in core of a carburizing 20CrNi2MoV bearing steel subjected to cryogenic treatment

Microstructure Evolution and Mechanical Properties of High-Temperature Carburized 18Cr2Ni4WA Steel

Composition Design of low alloy Low-temperature Cast Steel and Its mechanical Properties

Alloying induced by severe deformation and recovery treatment on low-carbon steel surface

Study on Integrated Plasticity of Low-carbon Low-alloy Steel During Intercritical Annealing Followed by Subcritical Annealing

Optimization of heat treatment process after vacuum carburizing of 18Cr2Ni4WA steel

Investigation on Multi-Element Ni–Cr–Mo–Cu Alloying Layer by Double Glow Plasma Alloying Technique

Surface modification of CoCrFeNi high entropy alloy by low-temperature gaseous carburization

Study of M50NiL steel under carburizing and nitriding duplex treatment