Abstract:Plasma nitriding is widely used in various industrial applications to improve surface hardness and wear properties. Especially for tool steels, it is also used to improve the support and adhesion of diamond-like carbon (DLC) coatings. The properties of the nitrided zone produced by plasma nitriding are influenced by the applied process parameter, in particular temperature and time. However, for high-alloy tool steels, a deeper understanding of the underlying diffusion processes of the nitrogen and the interaction with the existing microstructure, as well as the effects on the case depth is still lacking. Therefore, in this study, specimens of high-alloy tool steel X153CrMoV12 were plasma nitrided at varying temperatures (480 °C, 520 °C, 560 °C) and treatment times (2 h, 4 h, 16 h). The resulting nitrided zones were investigated by optical and scanning electron microscopy (OM and SEM), depth-dependent glow discharge optical emission spectroscopy (GDOES), X-ray diffraction (XRD), and hardness measurements to characterize their microstructure, chemical composition, and hardness depending on the process parameters. The distribution of carbides (M7C3), e.g., chromium carbides, affects the diffusion of the nitrogen and the layer growth. An increase of temperature and duration leads to an increased layer thickness. The composition of the compound layer is, e.g., influenced by the process parameters: ε nitrides (Fe2–3N) occurred preferentially at lower temperatures, while γ′ nitrides (Fe4N) appeared mostly at higher temperatures. In order to investigate the influence of the carbides of the high-alloy tool steel on the nitriding process, a new methodology was developed by means of finite element analysis (FE), which makes it possible to analyze this influence on the development of the nitrogen concentration profile. This methodology makes it possible for the first time to map the heterogeneous nitrogen evolution and distribution.

Low Temperature Nitriding of Metal Alloys for Surface Mechanical Performance

Microstructures and Mechanical Performance of Plasma-Nitrided Al 0.3 CrFe 1.5 MnNi 0.5 High-Entropy Alloys

Advances in Low-Temperature Nitriding and Carburizing of Stainless Steels and Metallic Materials: Formation and Properties

Solutions to improve surface hardness of stainless steels without loss of corrosion resistance

Nitriding behavior and corrosion properties of AISI 304L and 316L austenitic stainless steel with deformation-induced martensite

MECHANICAL AND CHEMICAL PROPERTIES OF LOW TEMPERATURE PLASMA SURFACE ALLOYED 316 AUSTENITIC STAINLESS STEEL

Microstructure evolution and mechanical performance of Cr-N/Al-Cr multilayer coatings produced by plasma nitriding Cr-coated Al alloy

Surface hardening of high modulus steels through carburizing and nitriding: First insights into microstructure property relationships

Low-Temperature Plasma Surface Modification of Medical Grade Austenitic Stainless Steel to Combat Wear and Corrosion

High Temperature Gas Nitridation and Wear Resistance of TiAl Based Alloys

Low-temperature plasma nitriding at 500°C on surface-nanocrystalline Ti–4Al–2V alloy

Material Influence on the Micropitting and Wear Resistance of Nitrided External and Internal Gears

Low-Temperature Plasma Nitriding of Martensitic and Austenitic Steels to Increase Tribocorrosion Resistance*

Tribological Studies of Plasma Source Ion Nitrided Low Alloy Tool Steel

Evolution of Microstructure and Hardness of the Nitrided Zone during Plasma Nitriding of High-Alloy Tool Steel

Corrosion Behavior on Orthopedic NiTi Alloy with Nanocrystalline/amorphous Surface

New Insights of Wear Behavior Analysis on Low Temperature Treated AISI 253MA Stainless steel Material by Gas Nitriding Process

Micro-/Meso-Structure Control of Multi-Hostmetal Alloys by Massive Nitrogen Supersaturation

Effects of Initial Microstructure on the Low-Temperature Plasma Nitriding of Ferritic Stainless Steel

Effect of Plasma Nitriding Pretreatment on the Mechanical Properties of AlCrSiN-Coated Tool Steels

Short time nitriding and nitrocarburizing of martensitic stainless steel