Abstract:In this study, we investigated the nitriding and laser quenching composite modified layers of 42CrMo steel. MATLAB was used to fit the nitrogen concentration distribution during nitriding, and the laser temperature field was fitted using ABAQUS finite element simulation software. Two groups of simulation results were integrated to fit the modified layer depth under different processes, and the nitriding and laser quenching experimental results were compared with the simulation results, which indicated that the simulation results agreed well with the experimental results. The depth of the nitriding–laser quenching composite layer greatly improved compared with the nitriding or laser hardening layers. The austenitizing temperature of the 42CrMo steel was reduced to 577 °C by nitriding. Therefore, the depth of the austenitized layer of the 42CrMo steel heated with the same laser power significantly increased. Under the same laser process conditions, more austenitic phase transformation was observed in the nitriding layer than in the non-nitriding layer, so martensitic phase transformation was more likely to occur in the subsequent cooling process. After plasma nitriding at 460 °C for 16 h and laser quenching, the modified layer depth of the 42CrMo steel reached 990 μm, and the average surface hardness of the 42CrMo steel reached 625 HV0.1. The friction coefficient of the modified layer was the lowest, with a value of 0.433, and the minimum wear value was 1.024 mm3. Double hardness and thickness of the modified layer could be obtained by nitriding and laser quenching composite processes.

Surface properties of low alloy steel treated by plasma nitrocarburizing prior to laser quenching process

Mechanism of Laser Carbonitriding Enhancing the Wear Resistance of 45# Steel

Numerical Simulation and Surface Properties of 42CrMo Steel Treated by Plasma Nitriding and Laser Quenching

Laser Quenching of Ionic Nitrided Steel: Effect of Process Parameters on Microstructure and Optimization

Microstructure refinement and properties of 1.0C-1.5Cr steel in a duplex treatment combining double quenching and laser surface quenching

Effect of laser shock peening on plasma nitriding microstructure and properties of H13 steel

Surface characteristic and wear resistance of QT-700-2 nodular cast iron after laser quenching combing with shot peening treatment

Kinetics analysis and enhancement mechanism of aluminum-enhanced plasma nitriding for 42CrMo steel

An environmental friendly plasma oxynitrocarburising technology with excellent performances

Microstructure and mechanical properties of surface layer of M50NiL steel plasma nitrided

A Novel Duplex Treatment of C20 Steel Combining Low-Pressure Carburizing and Laser Quenching

Effect of Compound Treatment of Laser Shock Peening and Nitriding on Wear Resistance of M50 Steel

Research on 40Cr Laser Quenching Process for Guide Rail

Microstructure modification and improving corrosion resistance of laser surface quenched nickel–aluminum bronze alloy

Surface Modification of Chromium–Nickel Steel by Electrolytic Plasma Nitriding Method

Effect of laser shock peening as a pretreatment on ion nitriding of precipitation hardened stainless steel

Nitrogen–carbon-induced Spinodal Structure in Plasma Nitrocarburized 38crmoal with Hollow Cathode Discharging

Effect of the carburized layer on the plasma nitriding behavior of duplex treated M50NiL steel

Mechanical and Wear Properties of 42CrMo Steel by Plasma Nitriding assisted Hollow Cathode Ion Source

Study on laser surface hardening process of 30CrMnSiNi2A ultra-high strength steel fabricated by laser deposition manufacturing