Nitrogen–carbon-induced Spinodal Structure in Plasma Nitrocarburized 38crmoal with Hollow Cathode Discharging

Zhehao Zhang,Zhengwei Wang,Minghao Shao,Yongyong He,Yang Li,Yulong Li,Guangyan Chen,Jianbin Luo

DOI: https://doi.org/10.1007/s10853-024-09982-x

IF: 4.5

2024-01-01

Journal of Materials Science

Abstract:The commonly utilized nitriding steel 38CrMoAl is employed for components subjected to low-impact loads but high wear. In this investigation, 38CrMoAl underwent plasma nitrocarburizing using a hollow cathode plasma source, with variations in gas ratios aimed at process optimization. The findings revealed a noteworthy influence of the NH3 to CO2 ratio on the phase composition and properties of the nitrocarburizing layers. Two distinct surface types were observed: one composed of ɛ-Fe2–3(N, C) and γ’-Fe4N and the other consisting of nitrogen-containing martensite with a small quantity of nitride. The surface comprising iron nitride was formed via downslope diffusion, leading to increased surface hardness through nitride formation. Nitrogen-containing martensite was formed via uphill diffusion due to spinodal decomposition, reinforced by mechanisms including fine-grain strengthening, solid-solution strengthening, secondary hardening during tempering, and the pinning effect of metal nitrides precipitated at the grain boundaries. The spinodal structure exhibited superior properties, with a wear rate of 1.26e − 8 mm3/Nm. Thermodynamic calculations confirmed that nitrogen diffusion facilitated spinodal decomposition by expanding the spinodal gap and reducing system energy. This study successfully overcame the performance constraints associated with such nitrided layers, which holds promise for applications to other nitride materials.