Tribological Properties of the Modified Layers Prepared on 38crmoal Steel by Plasma Nitrocarburized and Post-Sulfurized Method
Haichun Dou,Zhehao Zhang,Minyi Zhang,Zelong Zhou,Xuening Yi,Zhengwei Wang,Mingquan Jiang,Yongyong He,Yang Li
DOI: https://doi.org/10.1016/j.vacuum.2024.113473
IF: 4
2024-01-01
Vacuum
Abstract:The tribological properties of the different modified layers of plasma nitrocarburized and post-sulfurized on 38CrMoAl steel under oil lubrication were investigated, and the wear mechanism was proposed. The modified layers were prepared by the plasma nitrocarburized at 520 degrees C for 5 hand post-sulfurized at 160 degrees C for 1, 3, and 5 h. The morphology, phase structures, and composition were characterized by optical microscopy, scanning electron microscopy, energy-dispersive X-ray spectroscopy, three-dimensional white light interferometry, X-ray diffraction, high-resolution transmission electron microscopy, and X-ray photoelectron spectroscopy. The sliding- wear characteristics were investigated by ball-on-disk wear tests against GCr15 steel counterparts. The results show that the nitrocarburized layer mainly comprises epsilon-Fe2-3(N, 2-3 (N, C) and gamma '-Fe4(N, '-Fe 4 (N, C), with a surface hardness of 1250 HV0.1. 0.1 . The nitrocarburized treatment significantly improved the wear resistance of the 38CrMoAl steel. For the plasma nitrocarburized and post-sulfurized samples, a sulfurized layer mainly consisting of FeS and FeS2 2 was formed on the nitrocarburized layer. The wear mass loss and friction coefficient of the duplex samples are significantly reduced due to the thin FeS layer acting as a solid lubricant. A two-step method, plasma nitro- carburized and post-sulfurized duplex treatment, further improves tribological performance, which is crucial for engineering applications.