Effect of Additive Amount of Cr on Microstructure and Properties of Wc-9ni Cemented Carbides

Shi Kaihua,Zhou Kechao,Li Zhiyou,Zan Xiuqi,Min Zhaoyu,Liao Jun

2016-01-01

Rare Metal Materials and Engineering

Abstract:A series of WC-9Ni-xCr cemented carbides were prepared through a traditional powder metallurgy method. The effects of Cr additive amount on the microstructure and properties of WC-9Ni cemented carbides were investigated using X-ray diffraction, scanning electron microscope, mechanical property tester and immersion corrosion tests. The results show that Cr addition has an impact on the microstructure and mechanical properties' of the WC-9Ni cemented carbides. The trace addition of Cr inhibits the grain growth of the WC grains, decreases the density and bending strength of WC-9Ni cemented carbides, and increases the hardness and immersion corrosion resistance in neutral water of the alloys. With the Cr content increasing, the variation tendency of grain size, density, hardness, bending strength and corrosion resistance of the alloy slows down. Furthermore, extensive addition of Cr in WC-9Ni cemented carbides results in the formation of a new phase, (W-x,Cr(1-x))2C, which is easy to become a fracture source of the alloy. Combining the results of microstructure and properties, we conclude that sample 3# with Cr addition of 1.2 wt% exhibits a relatively optimal comprehensive performance in the five groups of samples.