Abstract:Joint homogenization during transition metal carbides ceramic bonding has attracted much attention as a technique to increase the service temperature and relieve the residual stress for various high-temperature applications. In this work, homogeneous joints of ZrC0.85 ceramic were obtained by diffusion bonding using single Nb and multiple Ti/Nb/Ti as the interlayer. The effect of interlayer composition, bonding temperature and holding time on the microstructure of the joints was investigated. The effect of Nb and Ti on the composition homogeneity and the formation of Kirkendall voids in the ZrC0.85 joints was also discussed. When using single Nb as the interlayer, the homogenization of the joints can be achieved at a bonding temperature of ∼1500 °C and holding for 1 h and no Kirkendall voids were observed when further increasing the bonding temperature to 1600 °C because of the good mutual solubility of NbCx and ZrCx and the relative moderate diffusion rate of Nb. However, severe Kirkendall effects were observed at a higher temperature of 1700 °C, which would deteriorate the high-temperature performance of the joints. The adoption of Ti/Nb/Ti further minished the diffusion rate difference of the interfacial elements through the formation of TiCx phase. As a result, only a few Kirkendall voids were formed at 1700 °C. Nano-hardness of the resultant homogeneous joints was comparable to that of the ZrC0.85 ceramic due to their similar composition. This study shows that active diffusion bonding based on interlayer design for homogeneous joints could pave a new way to join transition metal carbides.

Microstructure and Properties of the Diffusion Bonding Zrb2-Sic/Nb Joint

Diffusion bonding of ZrB2-SiC and Nb using dynamic compressed Ni foam interlayer

Diffusion bonding of ZrB 2-SiC/Nb with in situ synthesized TiB whiskers array

Microstructure Evolution and Its Effect on the Mechanical Properties of the ZrC–SiC Composite Joint Diffusion Bonded with Pure Ni Foil

Interfacial Microstructure and Properties of In-situ TiB Reinforced ZrB2-SiC Joints

Interface Homogenization Control and Microstructural Analysis of ZrC0.85 Joints Diffusion Bonded Using Nb and Ti/Nb/Ti As the Interlayer

Microstructure and mechanical properties of ZrB2-SiC joints fabricated by a contact-reactive brazing technique with Ti and Ni interlayers

Microstructures and mechanical property of ZrC joints diffusion bonded using Ti/Ta/Ti as the interlayer

Formation Mechanism of ZrC-SiC Joint Prepared by Pulsed-Current Assisted Diffusion Bonding

Partial Transient Liquid Phase Diffusion Bonding of ZrC-SiC and 304 Stainless Steel by Ti/Ni Interlayer: Microstructure and Properties

Microstructure and Mechanical Properties of ZrB2–SiC Ultrahigh Temperature Ceramic Composite Joint Using TiZrNiCu Filler Metal

Electroplating Assisted Diffusion Bonding of ZrC–SiC Composite for Full Ceramic Joints

Microstructure and mechanical properties of ZrB2-SiC ceramic composite brazed joint

Microstructures and Mechanical Property of ZrCx Joints Diffusion Bonded Using Ti/Ta/Ti As the Interlayer

Interfacial reaction evolution of the ZrC ceramic joint diffusion bonded with Ni interlayer

Cyclic Thermal Shock Behaviours of ZrB2-SiC Ultra-High Temperature Ceramics Joints Bonded with Ni Interlayer

Interfacial Microstructure and Joining Properties of TiAl/Ti3AlC2 Diffusion Bonded Joints Using Zr and Ni Foils As Interlayer

Microstructure and Mechanical Property of the Zrb2-Based Ultra-High-Temperature Ceramic Composites Brazed Joint

Effect of Zr on the solid sintering process of SiBCN ceramics: Diffusion couple method experiment and DFT calculation

Microstructural Evolution and Mechanical Properties of Zrb2-Sic/Cu/Ti/Ti6al4v Brazing Joints

Brazing ZrB2-SiC ceramics to Nb with a novel CoFeNiCrCu high entropy alloy