Interfacial reaction evolution of the ZrC ceramic joint diffusion bonded with Ni interlayer

Changbao Song,Peng He,Tiesong Lin,Dechang Jia

DOI: https://doi.org/10.1016/j.ceramint.2014.04.163

IF: 5.532

2014-01-01

Ceramics International

Abstract:ZrC ceramic was diffusion bonded with pure Ni as the interlayer to investigate its interaction mechanism. Results show that the Ni–ZrC interfacial reaction includes two characteristic stages: the solid phase diffusion and Ni–ZrC eutectic reaction. An atomic interdiffusion was observed during the solid phase diffusion stage and corresponding product was proven to be Ni-based solid solution, which transformed into Ni–Zr–C ternary eutectic around 1200°C. Hereafter, the interfacial reaction transformed into a liquid phase reaction, which was in fact a dissolution process of ZrC into the liquid. The formed Ni–Zr–C ternary eutectic liquid permeated into the porous ZrC ceramic, leading to the formation of a thick transition layer. During the cooling period, graphite crystallized first from the liquid due to the dissolution change of C element. Decreasing in temperature, ZrC particles recrystallized from the liquid and the residual liquid solidified into Ni-based solid solution.