Abstract:<p>Two FeCrAl alloy coatings with different Cr and Al contents were deposited on Zr-alloy substrates via the cold spray deposition method to study the efficacy of these coatings to improve the accident tolerance of Zr-alloy fuel cladding in light water reactors (LWRs). First, the coatings were tested in a 400°C steam autoclave for 72 hours as an accelerated method to simulate the normal LWR operating conditions. In these tests, both coatings resulted in notable improvements in oxidation resistance compared to the Zr-alloy, with the higher Cr containing coating exhibiting a thinner oxide layer. Both coatings provided good oxidation resistance when tested in 1200°C ambient air environment; however, the formation of a low melting point eutectic (∼928°C) between Fe and Zr resulted in significant melting associated with inter-diffusion between Fe in the coating and the Zr in the substrate. Therefore, to take advantage of the superior oxidation resistance that FeCrAl coatings can provide, a Mo interlayer was deposited, also by the cold spray process, in-between the protective FeCrAl coating and the Zr-alloy substrate, thus creating a dual cold spray layer accident tolerant coated cladding concept. The wear resistance of the FeCrAl coating was superior to the Zr-alloy substrate based on pin-on-disk wear tests, providing an indication of the benefits of such coatings to reduce grit-to-rod fretting (GTRF) damage. The feedstock powders, microstructure, phases, hardness of coatings, as well as oxide and inter-diffusion layers of oxidized coatings were examined using SEM, XRD, and XPS characterization techniques.</p>

Experimental kinetic study of interdiffusion behavior and intermetallic compound Zr(Fe,Cr)2 formation at the Cr/Zry4 interface under elevated temperatures

Interfacial Evolution in Cr/Mo-Coated Zr Alloys near the Mo-Zr Eutectoid Temperature

Microstructure evolution and mechanical property of high temperature solid-state diffusion bonded Cr-Zry4 with and without a 316 SS interlayer

Microstructure Evolution and Failure Mechanism of Cr-coated Zry-4 in Air and Steam at 1200 °C

Direct experimental evidence of the reduction of Cr2O3 by Zr at high temperature

Corrosion Degradation Mechanism of Cr-Coated Zr-4 Alloy under Simulated Nuclear Conditions for Accident-Tolerant Fuel

Interface stability and microstructural evolution of the (Cr/CrN)24-coated zirconium alloy under different thermal shock temperatures

Microstructure evolution and interdiffusion behaviour of Cr/Mo coated Zr-4 alloys at 1330 °C-1500 °C

Mechanical property and strengthening mechanism of ZrC nanoparticle dispersion-strengthened Mo containing FeCrAl alloys

From solid solution to cluster formation of Fe and Cr in $α$-Zr

A comprehensive experiments and calculations on the Cr/Zr interface behaviour of Cr coated Zr cladding

Evolution of Cr/Cr2O3 interface in Cr-coated zirconium alloy in high temperature steam

Investigation on Microstructures and High-Temperature Oxidation Resistance of Cr Coatings on Zircaloy-4 by Multi-Arc Ion Plating Technology

Experimental evaluation of cold spray FeCrAl alloys coated zirconium-alloy for potential accident tolerant fuel cladding

Xe20+ ions irradiation and autoclave corrosion coupled with steam oxidation behaviors of FeCrAlMoSiY-coated Zr claddings

Influence of Zr on grain orientation, texture, and mechanical properties in hot- and warm-rolled FeCrAl alloys

Systematic investigations on the oxidation mechanism of Cr coated Zr-4 alloy under different high-temperature steam conditions

An in-situ TEM investigation of microstructure evolution in Cr-coated zirconium alloy under heavy ion irradiation: Simultaneous evolution of both Cr coating and Zr-4 matrix

Radiation-Induced Sharpening in Cr-Coated Zirconium Alloy

Autoclave grid-to-rod fretting corrosion behaviors of the Zr alloy fuel cladding with and without Cr coating through advanced characterization

Tem Characterizations of a Zro2/Cr Composite Coating on Zr-1nb Alloy after 1200°C Steam Oxidation