Abstract:SiC ceramic was successfully brazed to Zircaloy-4 using Zr-24Ni (at.%) filler alloy for nuclear application. The wetting behavior and interfacial reaction between the Zr-Ni filler and SiC substrate were studied. The results showed that the Zr-Ni filler possessed excellent wettability (wetting angle ∼ 4°) on the SiC substrate, and the interfacial reaction products of ZrC and Zr2Si were formed. The effect of brazing temperature on the microstructure and shear strength of the SiC/Zircaloy-4 joint were investigated. When the brazing temperature was lower than 1060°C, the interface reaction of the joint was weak and the joint was mainly composed of SiC/ZrC/Zr2Ni +Zr-based solid solution/Zircaloy-4. When the brazing temperature was higher than 1060°C, the interface reaction was enhanced and the Zr2Si phase appeared in the joint. The maximum shear strength of the joint was 110 MPa at a brazing parameter of 1060°C for 15 min due to the moderate interface reaction between filler and substrates. Moreover, the experiment of He ion irradiation on the joint at room temperature showed that no significant irradiation damage appeared for SiC, ZrC and Zr2Ni in the joints when the irradiation fluence was lower than 1×1016 ions/cm2. However, when the irradiation fluence was higher than 5×1016 ions/cm2, the transformation of SiC and Zr2Ni from crystalline into amorphous state was observed. As the irradiation fluence increased, microcracks appeared in SiC and ZrC due to the uncoordinated irradiation swelling between them.

Electroplating Assisted Diffusion Bonding of ZrC–SiC Composite for Full Ceramic Joints

Study on interface behavior of Be/CuCrZr alloy by diffusion bonding

Research on Be/CuCrZr Bonding by Hot Isostatic Pressing at Intermediate Temperature

Reinforcement of ceramic bonded joints with intermetallic compounds

Ultrasonic-assisted transient liquid phase bonding of SiC ceramic and aluminum alloy using an inactive Zn interlayer

Ceramic Bonding and Joint'S Strengthening Through Forming Intermetallic Compounds in Situ

Effect of Zr addition on the interfacial reaction of the SiC joint brazed by Inconel 625 powder filler

An ultra-strength SiC ceramic joint with an in-situ formed high-entropy carbide interlayer via diffusion bonding by spark plasma sintering

Joining silicon nitride ceramics with ZrSi2-SiC composite filler by spark plasma sintering

Microstructures and mechanical property of ZrC joints diffusion bonded using Ti/Ta/Ti as the interlayer

Joining SiC ceramics with ZrSi2–SiC filler at low temperatures

Microstructure and shear strength of SiC/Zr joint brazed with LiAlSiO4/graphene-coated Cu-foam composite interlayer

TLP diffusion bonding of Si3N4 ceramics using Ti/Ni/Ti multilayer and controlling of joints＇ quality

Wetting and brazing of Cf/C composites with Si–Zr eutectic alloys: The formation of nano- and coarse-SiC reaction layers

Joints in Si_3N_4 Ceramics Bonded Using Solid-Liquid State Bonding with Intermetallic Compounds Formed in Situ

Mechanical property improvement of diffusion bonded ZrC x joints by chemical homogenization using Ta as the interlayer

Interfacial reaction mechanism of SiC joints joined by pure nickel foil

Effect of Brazing Parameters on the Microstructure and Properties of SiC Ceramic Joint with Zr-Cu Filler Metal

Bonding Ceramics with Al/Ti/Al Multilayers by in Situ Formation of Intermetallic Compound

Brazing ZrB2-SiC ceramics to Nb with a novel CoFeNiCrCu high entropy alloy

Brazing SiC ceramic to Zircaloy-4 using Zr-Ni filler alloy: Microstructure, mechanical properties and irradiation behavior