Abstract:Zirconium-based alloy is widely applied as the fuel cladding material. Its weld needs high precision and small deformation, so the low-temperature bonding is a crucial issue to be addressed. In this study, we used pure titanium interlayer to join Zr-4 alloys by diffusion bonding at low temperature. A sound joint with pure titanium interlayer was bonded at 680 °C, which was 70 °C lower than that of the direct bonding. The effect of welding parameters on the microstructure and phase composition was investigated by scanning electron microscope (SEM) with energy dispersive spectroscopy (EDS), and transmission electron microscope (TEM). Four solid solutions, (hexagonal close-packed) hcp-Ti 0.92 Zr 0.08 , hcp-Ti 0.7 Zr 0.3 , hcp-Ti 0.5 Zr 0.5 , and (body-centered cubic) bcc-Ti 0.5 Zr 0.5 , were identified forming at the Ti/Zr interface by EDS and TEM analysis. The nanohardness and Young's modulus were measured by nanoindentation. The highest and lowest nanohardness values across the joint were 5.65 GPa for the hcp-Ti 0.7 Zr 0.3 phase, and 4.09 GPa for the bcc-Ti 0.5 Zr 0.5 phase, respectively. The fracture initiated in the bcc-Ti 0.5 Zr 0.5 phase, prolonged at the Ti/Zr interface because of incoordination in the deformation process of two phases, and then the transverse tearing occurred in the hcp layer. The shear strength initially increased and then decreased as the increasing parameters. The maximum shear strength reached 255 MPa of the joint bonded at 750 °C for 60 min under 15 MPa. Besides, the formation mechanism of the Ti/Zr interface was revealed for the Zr-4 alloy joint with pure titanium interlayer.

Microstructures and Mechanical Property of ZrCx Joints Diffusion Bonded Using Ti/Ta/Ti As the Interlayer

Microstructures and mechanical property of ZrC joints diffusion bonded using Ti/Ta/Ti as the interlayer

Mechanical Property Improvement of Diffusion Bonded ZrCx Joints by Chemical Homogenization Using Ta As the Interlayer

Mechanical property improvement of diffusion bonded ZrC x joints by chemical homogenization using Ta as the interlayer

Interface Homogenization Control and Microstructural Analysis of ZrC0.85 Joints Diffusion Bonded Using Nb and Ti/Nb/Ti As the Interlayer

Research on Be/CuCrZr Bonding by Hot Isostatic Pressing at Intermediate Temperature

Cross-diffusion Phenomena Within a ZrCx – Zr – ZrCx Joint

Microstructure evolution of the Zr-4 alloy joints diffusion bonded with pure titanium interlayer and its influence on joint properties

Design of the Multiple Transition Metals Interlayer Process to Diffusion Bond ZrCx Ceramics

Microstructure and Mechanical Properties of Diffusion Bonded Joint of TC4 Alloy Using Zr as Interlayer

Interfacial Microstructure and Properties of In-situ TiB Reinforced ZrB2-SiC Joints

Microstructure Evolution and Mechanical Property of ZrC-SiC/Ti6Al4V Joints Brazed Using Ti-15Cu-15Ni Filler

Interfacial Microstructure and Mechanical Property of ZrC-SiC Ceramic and Ti6Al4V Joint Brazed with AgCuTi Alloy

Microstructural Evolution and Mechanical Properties of Zrb2-Sic/Cu/Ti/Ti6al4v Brazing Joints

Interfacial microstructure and mechanical property of ZrC-SiC ceramic and TiAl joint brazed with AgZr active filler metal

Microstructure and Properties of the Diffusion Bonding Zrb2-Sic/Nb Joint

Microstructure and Mechanical Properties of ZrB2–SiC Ultrahigh Temperature Ceramic Composite Joint Using TiZrNiCu Filler Metal

Microstructure Evolution and Bonding Mechanism of ZrO2 Ceramic and Ti-6Al-4V Alloy Joints Brazed by Bi2O3-B2O3-ZnO Glass Paste

Microstructure and mechanical properties of ZrB2-SiC joints fabricated by a contact-reactive brazing technique with Ti and Ni interlayers

Interfacial Microstructure and Joining Properties of TiAl/Ti3AlC2 Diffusion Bonded Joints Using Zr and Ni Foils As Interlayer

Microstructure evolution and mechanical properties of ZrO 2 /TiAl joints vacuum brazed by Ag–Cu filler metal