Abstract:Microstructure and high temperature oxidation behaviour of Ti45Al8Nb0.5B0.2C alloy was investigated in this work. XRD, SEM, TEM and EDS analysis demonstrate that as-cast Ti46Al8Nb0.5B0.2C alloy after HIP has fully lamellar microstructure consisting of gamma and alpha(2) with point-like or ribbon-like TiB2 distributing in the colony or at grain boundary. When the alloy was treated at 1400 degrees C for 1 h and oil cooled from the single alpha filed leads to alpha ->gamma(m) transformation and gamma(m) was aged in the alpha+gamma two-phase field, alpha plates precipitated on all {111} planes of the gamma(m), to form fine microstructures. In addition to determination of the oxidation knetics by mass gain measurements, surface and cross-sectional morphologies of oxidizing layer formed was observed by SEM and the present phases in the scales were analyzed by XRD. Results show that oxidation reaction constant and power index for Ti46Al8Nb0.5B0.2C alloy oxidized at 900 degrees C for 100 h were 0.00192 and 1.1381, respectively. However, oxidation reaction constant and power index for Ti46Al8Nb0.5B0.2C alloy oxidized at1000 degrees C for 100 h were 0.31637 and 2.0076, respectively. Oxidizing layer of Ti46A18Nb0.5B0.2C alloy after 900 degrees C, 100 h oxidation was about 4 mu m and composed of four layer. The first layer is discontinous Al2O3, the second layer is the mixture of Al2O3 and TiO2, and the last is rich in Nb. Oxidizing layer of Ti46Al8Nb0.5B0.2C alloy after 1000 degrees C, 100 h oxidation was about 5 mu m and composed of 4 layer. The first layer is TiO2, the second layer is the mixture of Al2O3 and TiO2, and the third layer is nitride layer in sequence.

Oxidation Behavior of Surface Plasma Niobium Alloying Layer on Ta2 at 700 Similar to 900 Degrees C

Thermal Oxidation Behaviour of Ti6Al7Nb and Ti6Al4V Alloys

Effect of Niobium Surface Alloying on the Antioxidation of Ti-6Al-4V

Oxidation Resistance of Ti-6Al-4V by Plasma Niobium Surface Alloying

Oxidation Behavior of Nb-Ti-Si-Cr Based Ultra-high Temperature Alloy at 1250℃

Study on Double-Glow Plasma Niobium Surface Alloying of Pure Titanium

High-Temperature Oxidation Behavior of Plasma Surface Nb-Cr-(Si) Alloying System on γ-TiAl

High-Temperature Oxidation of NbTi-Bearing Refractory Medium- and High-Entropy Alloys

High Temperature Oxidation Behavior of NiTiNb Intermetallic Alloys

Oxidation Behavior and Mechanism of a Ni-based Single Crystal Superalloy with Single Α-Al2o3 Film at 1000 °C

Influence of Temperature on Characteristics of TiAl Plasma Surface Niobiumizing

Plasma Alloying of Tial with Niobium and Its Wear Resistance

High Temperature Oxidation Behavior of Nb-Ti-Al Alloy and Its Silicide Coating

Study on the Oxidation Behavior of TiB2-CeO2-Modified (Nb,Mo,Cr,W)Si2 Coating on the Surface of Niobium Alloy

Oxidation Behavior and Oxide Scale Characteristics of TiAl-Nb Alloy with Full Lamellar Microstructure at High Temperature

Oxidation Behavior of a High-Nb-Containing TiAl Alloy with Multilayered Thermal Barrier Coatings

Initial Oxidation Behavior in Air of TiAl-2Nb and TiAl-8Nb Alloys Produced by Electron Beam Melting

On the high-temperature oxidation behavior of a niobium-bearing high nickel-chromium alloy: microstructural evolution and implications on oxidation mechanisms

Microstructure and high temperature oxidation behaviour of Ti45Al8Nb0.5B0.2C alloy

EFFECT OF Nb ON THE HIGH TEMPERATURE OXIDATION BEHAVIOR OF TiNiAl ALLOYS

Effect of Thermal Oxidation on the Surface Characteristics and Corrosion Behavior of a Ta-implanted Ti-50.6Ni Shape Memory Alloy