High temperature protection of a novel TiB 2 -modified (Nb,Mo,Cr)Si 2 ceramic coating on Nb-based alloy
Xiaojun Zhou,Jiawei Xu,Yitao Zha,Yafang Zhang,Guanzhi Deng,Xiaojun Zhao,Zhenyang Cai,Sainan Liu,Lairong Xiao
DOI: https://doi.org/10.1016/j.jeurceramsoc.2024.01.092
IF: 5.7
2024-02-26
Journal of the European Ceramic Society
Abstract:In order to solve the challenge of poor protection of conventional NbSi 2 coatings in high temperature oxidation environments, a new TiB 2 -modified (Nb,Mo,Cr)Si 2 composite ceramic coating was prepared on the surface of Nb521 substrate by triple slurry sintering method. The composite ceramic coating maintained the complete morphology after oxidation at 1600 °C for 15 h, due to the oxide layer TiO 2 -(Ti 0.6 Cr 0.2 Nb 0.2 )O 2 -SiO 2 formed on the coating surface, which could effectively reduce the volatilization behavior of SiO 2 and prolongue the oxidation life of the coating by wrapping the SiO 2 layer. In addition, the coating successfully withstood 1500 cycles from room temperature to 1600 °C, due to the fact that CrSi 2 and MoSi 2 significantly modulated the difference in thermal expansion coefficients between the Nb521 substrate and the NbSi 2 coating, making the thermal stress generated during the thermal shock cycle lower than the intrinsic strength of the coating.
materials science, ceramics