Formation and properties of niobium silicide coatings on Nb-Ta alloy substrate

Beatriz A. Pinto,Nabil Chaia,Ana Sofia C. M. D’Oliveira

DOI: https://doi.org/10.1177/09544062241299227

2024-12-01

Proceedings of the Institution of Mechanical Engineers Part C Journal of Mechanical Engineering Science

Abstract:Proceedings of the Institution of Mechanical Engineers, Part C: Journal of Mechanical Engineering Science, Ahead of Print. Niobium silicide coatings have been noted in the aeronautical and aerospace industries due to their high resistance to oxidation and creep. Despite these desirable properties, there is a need for further improvements to make them more applicable in demanding scenarios. This study investigates niobium silicide coatings processed on a Nb-22Ta alloy substrate by Double Pack Cementation method, to assess the influence of tantalum in coatings. The pack mixture was composed by 15% Si, 5% salt halide activator and 80% Al2O3, with NH4Cl and NH4F used as activators. The coatings were processed at 1000°C for 6 h. Analysis of the processed surfaces included a correlation with similar diffusion coatings processed on pure Nb under similar conditions. The results obtained by SEM and EDS revealed a low presence of Ta in the coatings, regardless of the halide activator used. Coatings processed with NH4F showed exclusive formation of NbSi2, while those processed with NH4Cl exhibited the presence of both Nb5Si3 and NbSi2. Nanohardness analysis indicated hardness levels of the niobium silicide coatings processed with NH4F similar to coatings processed with pure Nb substrate (1459 HV), different from the coatings processed with NH4Cl which demonstrate a much higher hardness close to the surface, around 2038 HV. Furthermore, coatings on Nb-22Ta exhibited better oxidation resistance at elevated temperatures, demonstrated by thermogravimetric analysis up to 1350°C. This behavior confirms s that silicide coatings are influenced by elements from the substrate Nb-22Ta that can be enhanced by processing conditions such as the activator in the pack mixture.

engineering, mechanical