Microstructure and High Temperature Properties of Nb2O5/TiO2 Coatings by Micro-arc Oxidation

Lu Xiaofeng

2023-01-01

Rare Metal Materials and Engineering

Abstract:To study the high temperature oxidation resistance of micro-arc oxidation coatings of Ti6Al4V titanium alloy, Nb2O5/TiO2 composite coatings were prepared by adding nano- Nb particles into sodium silicate electrolyte. The microstructure and phase composition of the coatings were analyzed by scanning electron microscopy (SEM) and X-ray diffractometry (XRD). The results show that with the increase in nano-Nb concentration, the micropores on the surface of the coatings increase in diameter and decrease in number. The content of Nb increases to 5at%, the thickness of the coatings increases from 42.28 mu m to 55.48 mu m. The coatings are composed of anatase TiO2, rutile TiO2, Al2TiO5, Nb2O5 and Nb-Ti compounds while the peak value of rutile TiO2 and Nb2O5 gradually increase. The mass gain of the sample decreases from 10.25 mg/cm(2) to 2.281 mg/cm(2) of the coatings with 6 g/ L Nb concentration, the average oxidation rate decreases from 2.8472x10(-5) mg center dot cm(-2) center dot s(-1) to 6.3361x10(-6) mg center dot cm(-2) center dot s(-1). The crack number of the coatings decrease with increasing the Nb concentration, which effectively improve the high temperature oxidation resistance of the coatings.