Abstract:To investigate the impact of Al and Nb elements on the formation of a protective oxide layer on the surface of Fe-35Ni-20Cr-xAl-yNb (x = 0, 2, 4, 6 wt.%; y = 0, 1, 2 wt.%) alloys, their oxidation behavior was examined at 1000 °C, 10−17 atm. and 10−25 atm. oxygen pressure, and the oxidation mechanism was analyzed by Factsage and Pandat calculations. Enhancing the Al content at 10−17 atm. inhibited the generation of FeCr2O4 on the alloy surface and increased the Al content in the M2O3 layer. When the Al content exceeded 6 wt.%, the oxide film partially peeled off. It was found that the addition of Nb increased the activity of Cr and Al and decreased the activity of Ni and Fe and promoted the formation of Al2O3, and the appearance of Nb2O5 in the subsurface layer increased the density of the oxide film. In addition, under an oxygen pressure of 10−25 atm., the only protective layer on the surface of the alloy comprised of Al2O3. The experimental results demonstrated that the Fe-35Ni-20Cr-4Al-2Nb alloy generated a continuous and dense Al2O3 protective film, and the reduction in oxygen pressure and the addition of Nb elements were favorable for selective external oxidation of Al2O3.
materials science, multidisciplinary,metallurgy & metallurgical engineering,physics, applied,chemistry, physical, condensed matter
What problem does this paper attempt to address?
The problem this paper attempts to address is the study of the effects of aluminum (Al) and niobium (Nb) elements on the pre-oxidation behavior of Fe-35Ni-20Cr-xAl-yNb alloy under low oxygen pressure conditions. Specifically, the authors explore through experiments and thermodynamic calculations how different contents of Al and Nb affect the formation of oxide layers on the alloy surface at 1000°C, 10⁻¹⁷ atm, and 10⁻²⁵ atm oxygen pressure, and how these elements influence the oxidation mechanism.
### Main Research Questions:
1. **Effects of Al and Nb on oxide layer formation**: Investigate how different contents of Al and Nb influence the formation of protective oxide layers on the alloy surface.
2. **Changes in oxidation behavior and products**: Analyze the changes in oxidation behavior and oxidation products of the alloy under different oxygen pressure conditions.
3. **Optimization of the best Al and Nb content**: Determine the optimal content of Al and Nb to achieve a continuous and dense Al₂O₃ protective film, thereby improving the oxidation resistance of the alloy.
### Research Background:
- **Oxidation resistance in high-temperature environments**: Fe-Ni-Cr-based alloys are widely used as high-temperature structural materials in high-temperature furnaces and refining equipment, requiring good oxidation resistance.
- **Comparison of Cr₂O₃ and Al₂O₃**: Traditional Fe-Ni-Cr alloys improve oxidation resistance by rapidly forming a surface Cr₂O₃ oxide layer, but Cr₂O₃ continues to oxidize at high temperatures to form volatile CrO₃, whereas Al₂O₃ has a lower growth rate and better thermal stability.
- **Role of Al and Nb**: Al can promote the formation of Al₂O₃, while Nb can increase the activity of Cr and Al, reduce the activity of Ni and Fe, and promote the formation of Al₂O₃. However, excessive Nb can lead to the formation of Nb₂O₅, which reduces the oxidation resistance of the alloy.
### Experimental Methods:
- **Material preparation**: Using high-purity Fe, Ni, Cr, Al, and Nb metal particles, alloy samples with different Al and Nb contents were prepared by vacuum arc melting.
- **Pre-oxidation experiments**: Pre-oxidation experiments were conducted at 1000°C, 10⁻¹⁷ atm, and 10⁻²⁵ atm oxygen pressure to observe oxidation products and oxidation behavior.
- **Characterization methods**: Scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS), and X-ray diffraction (XRD) were used to analyze the morphology, chemical composition, and phase composition of the oxide film.
### Conclusions:
- **Effect of Al content**: Increasing Al content can inhibit the formation of FeCr₂O₄ and increase the Al content in the M₂O₃ layer, but when the Al content exceeds 6 wt.%, the oxide film partially peels off.
- **Effect of Nb content**: Adding Nb can increase the activity of Cr and Al, reduce the activity of Ni and Fe, promote the formation of Al₂O₃, and form Nb₂O₅ in the sub-surface layer, increasing the density of the oxide film.
- **Optimal combination**: The Fe-35Ni-20Cr-4Al-2Nb alloy formed a continuous and dense Al₂O₃ protective film at 1000°C, 10⁻²⁵ atm oxygen pressure, exhibiting excellent oxidation resistance.
This study provides further reference for the research of AFA alloys, especially in optimizing the content of Al and Nb to improve the oxidation resistance of the alloy.