High-Temperature Oxidation Resistance of High-Nb TiAl-Based Alloy

Xf Ding,Y Shen,Xm Wang,Y Tan,Fg Wang

DOI: https://doi.org/10.3969/j.issn.1005-4537.2004.04.003

2004-01-01

Abstract:Four alloys were got by adding W, Cr into the equal atom-ratio TiAl-based intermetallic compound with high Nb concent. The interrupted oxidation behavior of the four alloys at 1000degreesC in static air was studied. The results show that addition of 14.3% Nb enhances the oxidation resistance of the alloy greatly and promotes the formation of continuous and compact Al2O3 oxide scale. The addition of W in the high-Nb alloy results more formation of P phase in the alloy, which impairs the beneficial effect of Nb. The addition of Cr makes the adhesiveness between oxide and matrix weaked; the formed oxide is liable to break off due to thermal stress during cooling. The influence of alloying elements on the oxidation resistance of the alloy is not simple superposition of the amount.