Abstract:TiO2-ZrO2 (Ti-Zr) carrier was prepared by a co-precipitation method and 1 wt. % V2O5 and 0.2 CeO2 (the Mole ratio of Ce to Ti-Zr) was impregnated to obtain the V2O5-CeO2/TiO2-ZrO2 catalyst for the selective catalytic reduction of NOx by NH3. The transient activity tests and the in situ DRIFTS (diffuse reflectance infrared Fourier transform spectroscopy) analyses were employed to explore the NH3-SCR (selective catalytic reduction) mechanism systematically, and by designing various conditions of single or mixing feeding gas and pre-treatment ways, a possible pathway of NOx reduction was proposed. It was found that NH3 exhibited a competitive advantage over NO in its adsorption on the catalyst surface, and could form an active intermediate substance of -NH2. More acid sites and intermediate reaction species (-NH2), at lower temperatures, significantly promoted the SCR activity of the V2O5-0.2CeO2/TiO2-ZrO2 catalyst. The presence of O2 could promote the conversion of NO to NO2, while NO2 was easier to reduce. The co-existence of NH3 and O2 resulted in the NH3 adsorption strength being lower, as compared to tests without O2, since O2 could occupy a part of the active site. Due to CeO2’s excellent oxygen storage-release capacity, NH3 adsorption was weakened, in comparison to the 1 wt. % V2O5-0.2CeO2/TiO2-ZrO2 catalyst. If NOx were to be pre-adsorbed in the catalyst, the formation of nitrate and nitro species would be difficult to desorb, which would greatly hinder the SCR reaction. All the findings concluded that NH3-SCR worked mainly through the Eley-Rideal (E-R) mechanism.

Simultaneous Selective Catalytic Reduction of NO and N2O by NH3 over Fe-Zeolite Catalysts

Tailoring the Proceeding of the NH3-SCO and NH3-SCR Reactions over FeOx Catalysts by Modifying with NbOx

In Situ DRIFTS Studies of NH3-SCR Mechanism over V2O5-CeO2/TiO2-ZrO2 Catalysts for Selective Catalytic Reduction of NOx

Selective Catalytic Reduction of NOx with NH3 over Short-Range Ordered W-O-Fe Structures with High Thermal Stability

Improvement of Catalytic Activity over Cu-Fe Modified Al-Rich Beta Catalyst for the Selective Catalytic Reduction of Nox with Nh3

Catalytic Performance of Fe–ZSM-5 Catalysts for Selective Catalytic Reduction of Nitric Oxide by Ammonia

Fe-doped Beta zeolite from organotemplate-free synthesis for NH3-SCR of NOx

Selective catalytic reduction of NO over Fe-ZSM-5: mechanistic insights by operando HERFD-XANES and valence-to-core X-ray emission spectroscopy

Selective Catalytic Reduction of NOxwith Ammonia over Fe-Mo/ZSM-5 Catalysts

Capability of molecular sieve-supported FeSO_4 catalyst for selective catalytic reduction of NO_x

Selective Catalytic Reduction of NO with NH3 over Mn–Fe/USY under Lean Burn Conditions

Optimizing Selective Catalytic Reduction of NO with NH3 on Fe2O3/WO3 Via Redox‐Acid Synergy

Kinetics of Selective Catalytic Reduction of NO by NH3 on Fe-Mo/ZSM-5 Catalyst.

Influence of Fe–Cu-SSZ-13 and hybrid Fe–Cu-SSZ-13 zeolite catalyst in ammonia-selective catalytic reduction (NH3-SCR) of NOx

High Activity and Wide Temperature Window of Fe‐Cu‐SSZ‐13 in the Selective Catalytic Reduction of NO with Ammonia

Selective Catalytic Reduction of NOx by Hydrocarbons over Copper-Free Metal Supported Zeolite

Cu/Fe-UZM-35 Catalysts for NOx Abatement in Diesel Vehicles for Next-Stage Emission Standards

Novel FeVO4 catalyst modified with NbTiOx for efficient selective catalytic reduction of NOx with NH3

Facile preparation of Fe-Beta zeolite supported transition metal oxide catalysts and their catalytic performance for the simultaneous removal of NO x and soot

Selective Catalytic Reduction of NO x by Methanol on Metal-Free Zeolite with Brønsted and Lewis Acid Pair

Recent advancements in Fe-based catalysts for the efficient reduction of NOx by CO