Effect of Thermo-mechanical Treatment on Microstructure and Properties of Cu-15Ni-8Sn Alloy
Xing Yan,Li Zhou,Gan Xueping,Li Si,Zhang Yang,Zhang Xianwei,Song Kexing
2018-01-01
Rare Metal Materials and Engineering
Abstract:The effect of homogenizing annealing and thermo-mechanical treatment processes on microstructure and properties of Cu-15Ni-8Sn-1.0Zn-0.8Al-0.2Si alloy was investigated using mechanical property test, electrical conductivity measurement, optical microscopy, scanning electron microscopy and transmission electron microscopy. The alloy ingot was treated by two-stage homogenizing annealing at 830 degrees C/2 h+850 degrees C/2 h, hot rolled by 70%, then solution treated at 850 degrees C for 1 h, followed by 60% cold-rolling deformation and aging treatment at 400 degrees C and 450 degrees C. Results show that after aging at 450 degrees C for 30 min, the hardness is 3780 MPa, electrical conductivity is 8.0% IACS, tensile strength is 1144 MPa, yield strength is 1098 MPa, and elongation is 3.29%. After aging at 400 degrees C for 1 h, the hardness is 3900 MPa, electrical conductivity is 7.4% IACS, tensile strength is 1164 MPa, yield strength is 1112 MPa, and elongation is 3.05%. The combined effects of spinodal decomposition strengthening, precipitation strengthening and substructure strengthening are the main strengthening mechanism in alloy. Meanwhile, the solid solubility of matrix is reduced, and the electrical conductivity of alloy is improved due to the precipitation of solute atoms. After two-stage homogenizing annealing treatment, the microstructure of the alloy is homogeneous equiaxed grain. It is found that spinodal decomposition and L1(2) ordering (beta-Ni3Sn) appear in the alloy during aging at 400 degrees C for 1 h. The crystal orientation relationships between copper matrix and beta-Ni3Sn precipitates are determined as: (00(2)over-bar)(cu) parallel to (00(1)over-bar)(beta,) [110](cu) parallel to [110](beta) ; ((2)over-bar20)(cu) parallel to ((1)over-bar10)(beta), [112](cu) parallel to [112](beta).