Strength and Plasticity Improvement of AZ31 Sheet by Pre-Inducing Large Volume Fraction of {10–12} Tensile Twins

Huihui Nie,Xinwei Hao,Xiaoping Kang,Hongsheng Chen,Chengzhong Chi,Wei Liang

DOI: https://doi.org/10.1016/j.msea.2020.139045

2020-01-01

Abstract:The major obstacle that limits the extensive application of Mg alloys is their poor ductility at room and low temperatures due to the inability of the < a > slip to accommodate the c-axis plastic strain. Although, inducing tensile twins (TTs) into Mg sheets can effectively overcome this problem most of the methods that are commonly employed for the induction of twins such as cold rolling and pre-compression are limited by the sheet size. Hence, a novel method known as the corrugated wide limit alignment (CWLA), was proposed to introduce a large volume fraction of TTs in Mg sheet of large dimensions. The evolution of microstructure and mechanical properties of as-rolled and CWLA-ed samples after cycle I and cycle II were examined as part of this study. A large number of TTs were observed in the CWLA-ed Mg sheet, and the fraction increased as increasing compressive strain, which effectively subdivided the original coarse grains. The grains were further refined by extensive dynamic recrystallization (DRX) that occurred at twin intersections and grain boundaries. Refinement strengthening and working hardening were responsible for improving the strength of the Mg sheet, and simultaneously, the ductility was also enhanced owing to the softening effect of DRX and twinning. Although twinning played a significant role in accommodating deformation during its initial stage, competing DRX and dislocation became the main ways to achieve deformation compatibility in the latter stage as the strain increased.