Abstract:Although <math>{101¯2}</math> twinning behavior has been extensively studied, it has rarely been investigated under biaxial tension. In the present research, the mechanical response and <math>{101¯2}</math> twinning behavior of a Mg AZ31 sheet under biaxial tension with various stress ratios (<math>σND:σTD</math>) along the normal direction (ND) and transverse direction (TD) were systematically studied. The results indicate that the yield stress along the ND is nearly independent of <math>σND:σTD</math>. Schmid law applied to <math>{101¯2}</math> twinning under biaxial tension yields better efficiency than that for uniaxial tension, and a higher efficiency is observed with a larger stress ratio along the TD; the fraction of experimentally observed twin variants with Schmid factors (SFs) of ranks 1 and 2 is approximately 45% for uniaxial tension, whereas it is approximately 68% for <math>σND:σTD=2:1</math> and approximately 88% for <math>σND:σTD=1:2</math>. This result contradicts with the previously reported result that Schmid law is more efficient for uniaxial stress states than under multiaxial stress conditions. It is found that biaxial tension will increase the difference in SF for the six twin variants and make Schmid law more efficient. Twin variant selection and volume fraction are highly dependent on <math>σND:σTD</math>. For uniaxial tension, the activities for the six variants are similar, and the (0002) poles of the twins are distributed evenly on a circle approximately 80°–90° away from the ND. In contrast, the variants <math>(01¯12)[011¯1]</math> and <math>(011¯2)[01¯11]</math> are more favorable under biaxial tension, and more (0002) poles of the twins concentrate around the rolling direction with a higher ratio of <math>σTD</math>. At a similar strain level, the twin fraction under biaxial tension is often different from that under uniaxial tension, and this difference varies with <math>σND:σTD</math>. This mechanism is associated with a stress-ratio-mediated detwinning behavior under biaxial tension. The findings in the present study provide a new and significant understanding of the twinning behavior of Mg alloys.

On the Strengthening and Slip Activity of Mg-3Al-1Zn Alloy with Pre-Induced { 10 1 over Bar 2 } Twins

On the Strengthening and Slip Activity of Mg-3Al-1Zn Alloy with Pre-Induced {101¯2} Twins

On the strengthening and slip activity of Mg-3Al-1Zn alloy with pre-induced { 10 1 ̄ 2 } twins

Activation of multiple twins by pre-tension and compression to enhance the strength of Mg–3Al–1Zn alloy plates

Numerical simulation of plastic behavior and meso inhomogeneous deformation in AZ31 Mg alloy

Effect of pre-deformation on the activation stress of {10–12} twinning in Mg–3Al–1Zn alloy

Identification and Analysis of Anomalous {101‾2} Twins in an Extruded Mg-2wt%Y Alloy Sheet During Uniaxial Tensile Loading

Strengthening Against {10(1)Over-Bar2} Twinning By Discontinuous And Continuous Precipitate In A Strongly Textured Mg-9al Alloy

{ 10 1 ̄ 2 } twinning behavior under biaxial tension of Mg–3Al–1Zn plate

{101¯2} Twinning Behavior under Biaxial Tension of Mg–3Al–1Zn Plate

Strengthening Against {101¯2} Twinning by Discontinuous and Continuous Precipitate in a Strongly Textured Mg-9Al Alloy

Simultaneous Enhancement of Strength and Ductility for AZ31 Magnesium Alloy by Pre-Twinning Induced Heterostructure

{10(1)Over-Bar2} - {10(1)Over-Bar2} Double Tensile Twinning In A Mg-3al-1zn Alloy Sheet During Cyclic Deformation

The Dislocation-Twin Interaction and Evolution of Twin Boundary in AZ31 Mg Alloy

Ductility Improvement by Twinning and Twin–slip Interaction in a Mg-Y Alloy

Influence of Basal Slip Activity in Twin Lamellae on Mechanical Behavior of Mg Alloys

The Interrupted Properties of an Extruded Mg Alloy

Influence of In-Plane Simple Shear Strain on the Grain Orientation Regulation and Stretch Formability of Pre-twinned AZ31 Magnesium Alloy Sheet

Mechanical Behavior and Microstructural Evolution in Rolled Mg-3Al-1Zn-0.5Mn Alloy under Large Strain Simple Shear

Twinning-mediated Plasticity by a Novel Multistage Twinning Mode in an Mg-Al-Gd Alloy

Mg-3Al-1Zn alloy deformed along different strain paths: Role of latent hardening