Abstract:The effect of major constituents (the Li content increases from 0.5 to 3 wt% and the Cu content decreases from 4.5 to 2 wt%) on microstructure and mechanical properties of cast Al-Li-Cu-Zr alloy were studied to understand a qualitative assessment of sequence and kinetics of multiple precipitations. Increasing the Li content progressively raises the melting temperature from 520 °C in 1# alloy (Al-0.5Li-4.5Cu, wt%) and 2# alloy (Al-1Li-4.5Cu) to 560 °C in 6# alloy (Al-3Li-2Cu). In addition, the variations of the major constituents result in the changes of the type and volume fraction of the inter- and intra-granular intermetallic phases. TEM results indicate that minor modifications to alloy composition greatly alter precipitation behavior during isothermal aging. The Li-poor alloy (2# alloy) presents a much shorter incubation time of T1-Al2CuLi precipitate than the Li-rich alloy (Al-1.5Li-4.5Cu, 3# alloy), while the nucleation of θ'-Al2Cu precipitate is promoted in Li-rich alloy. No typical spherical δ'-Al3Li precipitate is observed in 2# and 3# alloys during isothermal aging, except for the as-quenched 3# alloy. The preferential nucleation of δ' precipitate on the coherent and broad face of θ' precipitate is observed in 2# and 3# alloys, leading to the formation of "sandwich-like" δ'/θ'/δ' phases. Further decreasing Cu content to 2 wt% and increasing Li content to 3 wt% (6# alloy), the predominant phase in the matrix is δ' precipitate, accompanied by a small amount of unevenly distributed θ' and T1 precipitates. The best balance between ductility and strength is obtained by 2# alloy aged for 32 h, but 6# alloy has significant advantages in terms of density (2.437 g/cm3) and elastic modulus (82.65 GPa) over 2# alloy (density: 2.675 g/cm3; elastic modulus: 75.45 GPa).

Effects of Sc and Zr Addition on Microstructure and Mechanical Properties of Al-3Cu-2Li Alloy

Effects of Zr and Mg alloying on microstructure and properties of Cu-Cr-Si alloys

Effects of Sc and Zr microalloying on the microstructure and mechanical properties of high Cu content 7xxx Al alloy

Effects of Cr and Zr additions on the microstructure and properties of Cu-6wt.% Ag alloys

Microstructures evolution and mechanical properties disparity in 2070 Al-Li alloy with minor Sc addition

EFFECT OF Sc ON MICROSTRUCTURE AND PROPERTIES OF Al-Li-Cu-Mg-Zr ALLOY

Influence of Zr content on microstructure and mechanical properties of As-cast Al-Zn-Mg-Cu alloy

Microstructural evolution, precipitation behavior and mechanical properties of a novel Al–Zn–Mg–Cu–Li–Sc–Zr alloy

Effect of Zr addition on the microstructure evolution and mechanical properties of extruded Al-Cu-Li-Mn alloys

Microstructural evolution and mechanical properties of cast Al‐2.6Li‐2.8Mg‐(0.5, 1.4)Cu‐0.2Zr‐0.2Sc alloys during heat treatment

Effect of aging on the mechanical properties and corrosion susceptibility of an Al-Cu-Li-Zr alloy containing Sc

Influences of different Zr/Sc ratios on microstructure and mechanical properties of Al-2Si alloy

Effect of Rolling Reduction on Microstructures and Mechanical Properties of Sc-Containing Al-3.2Cu-1.5Li Alloy

Effect of Minor Sc Addition on the Microstructure Evolution of Al–Cu–Li–Mg Alloy During Homogenization with Different Cooling Modes

Influence of Sc and Zr additions on microstructure and properties evolution of Al–Zn–Mg alloy

The effect of major constituents on microstructure and mechanical properties of cast Al-Li-Cu-Zr alloy

Effects of addition of Er and Zr on microstructure and mechanical properties of Al–Cu–Mn–Si–Mg alloy

Effect of Rolling Temperature on Microstructure and Properties of Al-Mg-Li Alloy

Effect of heat treatments on microstructure and mechanical properties of sand cast Al–2Li–2Cu–0.5Mg–0.2Sc–0.2Zr alloy

Effect of scandium on microstructure and mechanical properties of high zinc concentration aluminum alloys

Enhancing the strength of Sc-containing Al-Cu-Li alloys by modifying the precipitation behavior through plastic deformation and heat treatment