Microstructure and Mechanical Properties of ZrC Coating on Zirconium Fabricated by Interstitial Carburization
Ziyuan Zhao,Fuyuan Liu,Qin Wang,Junming Li,Lisheng Zhong,Yunhua Xu,Pengfei Hui,Jianlei Zhu,Fuxue Yan,Mingxuan Zhao
DOI: https://doi.org/10.1016/j.jallcom.2020.155110
IF: 6.2
2020-01-01
Journal of Alloys and Compounds
Abstract:Herein, ZrC coating was fabricated on the surface of zirconium via interstitial carburization. High-carbon steel was selected as the carbon source to supply the interstitial carbon atoms and was hot-pressed with zirconium substrate at 1150 degrees C and uniaxial pressure of 2 MPa. The interstitial carbon atoms diffused into the surface of Zr forming a ZrC coating. The microstructure of the coating was characterized using X-ray diffraction (XRD), scanning electron microscopy (SEM), and electron backscattered diffraction (EBSD). The obtained coating was completely dense and pure ceramic, consisting of a single ZrC phase with a volume fraction of 100%. The diameter of ZrC grains exhibited a gradient distribution with a range of 180 nm to 5.9 mu m. The thickness of the coating was proportional to the square root of the carburizing time, following the classical parabolic law, reaching a coating thickness of 7.2 mu m after carburizing for 10 h. The microhardness tested on the coating surface reached 1500 HV and nanohardness measured on the cross-section of the ZrC coating reached 27 GPa, displaying a remarkable improvement compared to the zirconium substrate (192 HV and 3.6 GPa). The average fracture toughness of ZrC coating measured via Vickers indentation was 1.9 MPa.m(1/2). In response to a scratch where the scratch load increased linearly from 0 to 100 N, the coating demonstrated excellent adhesion with the substrate. As per the obtained results, we expect that the interstitial carburization method can also be applied to various Zr-based alloys. (C) 2020 Elsevier B.V. All rights reserved.