Abstract:Herein, ZrC coating was fabricated on the surface of zirconium via interstitial carburization. High-carbon steel was selected as the carbon source to supply the interstitial carbon atoms and was hot-pressed with zirconium substrate at 1150 degrees C and uniaxial pressure of 2 MPa. The interstitial carbon atoms diffused into the surface of Zr forming a ZrC coating. The microstructure of the coating was characterized using X-ray diffraction (XRD), scanning electron microscopy (SEM), and electron backscattered diffraction (EBSD). The obtained coating was completely dense and pure ceramic, consisting of a single ZrC phase with a volume fraction of 100%. The diameter of ZrC grains exhibited a gradient distribution with a range of 180 nm to 5.9 mu m. The thickness of the coating was proportional to the square root of the carburizing time, following the classical parabolic law, reaching a coating thickness of 7.2 mu m after carburizing for 10 h. The microhardness tested on the coating surface reached 1500 HV and nanohardness measured on the cross-section of the ZrC coating reached 27 GPa, displaying a remarkable improvement compared to the zirconium substrate (192 HV and 3.6 GPa). The average fracture toughness of ZrC coating measured via Vickers indentation was 1.9 MPa.m(1/2). In response to a scratch where the scratch load increased linearly from 0 to 100 N, the coating demonstrated excellent adhesion with the substrate. As per the obtained results, we expect that the interstitial carburization method can also be applied to various Zr-based alloys. (C) 2020 Elsevier B.V. All rights reserved.

Microstructure and micro-mechanical properties of zirconia coating by atmospheric pressure chemical vapor deposition

Deposition Kinetics and Microstructure of APCVD ZrC Coating

Microstructure Characteristics of ZrO2 Coating Produced by Atmospheric Pressure Chemical Vapor Deposition

Microstructures and Ablative Properties of ZrC Coating by Chemical Vapor Deposition

Phase composition, microstructure and mechanical properties of ZrC coatings produced by chemical vapor deposition

Preparation and Microstructure of ZrC Coatings for C/C Composites

Microstructure and Mechanical Properties of ZrC Coating on Zirconium Fabricated by Interstitial Carburization

Effect of Deposition Parameters on Morphology and Composition of Chemical Vapor Deposited ZrC Coatings

Mechanical Properties and Residue Stress of Four Kinds of ZrC Coatings Prepared by Chemical Vapor Deposition

Microstructure Characteristics and Ablation Behavior of an Al1.92 Cr0.08 O3-SiC-ZrC Anti-Ablation Coating

Microstructure and Properties of ZrC-SiC Multi-Phase Coatings Prepared by Thermal Evaporation Deposition and an In-Situ Reaction Method

Microstructure Analysis of Zirconium Carbide Layer on Pyrocarbon-Coated Particles Prepared by Zirconium Chloride Vapor Method

Effect of temperature-dependent nano SiC on the ablation resistance of ZrC coating

Microstructural Control of Zirconium Carbide Coating Prepared by Chemical Vapor Deposition

High-temperature Oxidation of Sprayed Alumina and Zirconium‑yttrium-Based Coatings on Zircaloy-4 in Air and Oxygen: Investigation on Microstructure Evolution and Phase Changes

Microstructure, surface stress and surface temperature response of ZrB2–SiC based coatings

Chemical Vapor Deposition (CVD) of ZrC Coatings from ZrCl 4 -C 3 H 6 -H 2

Preparation of ZrC nano-particles reinforced amorphous carbon composite coating by atmospheric pressure chemical vapor deposition

Microstructure and High Temperature Anti-Ablation Behavior of Cr-modified ZrC Coating for SiC-coated Carbon/carbon Composites

Deposition Mechanism for Chemical Vapor Deposition of Zirconium Carbide Coatings

Effect of the Surface Microstructure of Sic Inner Coating on the Bonding Strength and Ablation Resistance of Zrb2-Sic Coating for C/C Composites