Electrochemical Fabrication of Highly Ordered Zro2-Hfo2 Binary Oxides Nanotube Arrays

Lingjie Li,Jing Xu,Jinglei Lei,Jianxin He,Jiarui Zhang,Nianbing Li,Shengtao Zhang
DOI: https://doi.org/10.14233/ajchem.2014.17489
2014-01-01
Abstract:The present work demonstrates a facile approach to fabricate highly ordered nanotubular ZrO2-HfO2 binary oxides. Zr-Hf alloy was electrochemically anodized in an ethylene glycol electrolyte containing small amounts of fluoride via a two-step process. The field emission scanning electron microscopy images show the highly ordered nanotube arrays with a length of approximately 6.8 mu m, an average diameter of approximate 32 nm and a tube density of 3 x 10(10) cm(-2) were formed on the Zr-Hf alloy surface. X-ray photoelectron spectroscopy analysis provides evidence that the composition of the formed nanotubes is ZrO2-HfO2 binary oxides. X-ray diffraction studies indicates that monoclinic ZrO2 and HfO2 with small amount of tetragonal phase ZrO2 coexist in the nanotubular binary oxides layer after thermal annealing at 400 degrees C for 3 h. The present electrochemical approach can be extended to prepare the highly ordered nanotubular oxides with a wide range of composition and functionalities.
What problem does this paper attempt to address?