Abstract:Large-scale arrayed ZnO crystals with a series of novel morphologies, including tower-like, flower-like, and tube-like samples, have been successfully fabricated by a simple aqueous solution route. The morphology and orientation of the obtained ZnO crystal arrays can be conveniently tailored by changing the reactants and experimental conditions. For example, the tower-like ZnO crystal arrays were obtained in a reaction solution system including zinc salt, ammonia, ammonium salt, and thiourea, and the orientation of these tower-like crystals could be controlled by the contents of these reactants. Flower-like ZnO arrays were obtained at lower temperatures, and tube-like ZnO arrays were obtained by ultrasonic pretreatment of the reaction system. The growth mechanism of the tower-like and tube-like ZnO crystals was investigated by FESEM. The results show that tower-like crystals grow layer by layer, while tube-like crystals grow from active nanowires. Ultrasonic pretreatment is proved to be effective in promoting the formation of active nuclei, which have important effects on the formation of the tube-like ZnO crystals. In addition, large-scale arrays of these ZnO crystals can be successfully synthesized onto various substrates such as amorphous glass, crystalline quartz, and PET. This implies this chemical method has a wide application in the fabrication of nano-/microscale devices.

Arrays of ZnO Nanowires Fabricated by a Simple Chemical Solution Route

Conversion of large-scale oriented ZnO rod array into nanotube array under hydrothermal etching condition via one-step synthesis approach

Preparation of Large-Scale Highly Oriented Zno Noodle Arrays and Study on the Photoconductivity

Hydrothermal Synthesis of Well-Aligned ZnO Nanorod Arrays on Silicon

Large-scale fabrication of tower-like, flower-like, and tube-like ZnO arrays by a simple chemical solution route

Fabrication of ZnO/Al2O3 core–shell nanostructures and crystalline Al2O3 nanotube

Growth of Arrayed ZnO Nanowires Using a Solution Method

Controllable Assembly of Aligned ZnO Nanowires/belts Arrays.

Fabrication and Morphology of ZnO Nanorods Array Prepared from Aqueous Solution under an Assisted Electrical Field

Carbon-Assisted Synthesis of Aligned Zno Nanowires

Fabrication and characterization of hexagonally patterned quasi-1D ZnO nanowire arrays

Synthesis of Monodispersed Zno Nanorod Array Films by Chemical Solution Deposition.

Aligned ZnO Nanorod Arrays Fabricated on Si Substrate by Solution Deposition

Sequential Occurrence of ZnO Nanopaticles, Nanorods, and Nanotips During Hydrothermal Process in a Dilute Aqueous Solution

ZnO Nanorod Arrays: Field-assisted Growth in Aqueous Solution and Field Emission Properties

Zinc Oxide Nanostructure Fabricated In Anodic Alumina Oxide Template By Sol-Gel Method

A simple route to scalable fabrication of perfectly ordered ZnO nanorod arrays

ZnO nanotubes by template-assisted sol–gel route

Growth of Arrayed Nanorods and Nanowires of ZnO from Aqueous Solutions

Fabrication and characterization of single-crystalline ZnTe nanowire arrays

Fabrication of Arrays of Zinc Oxide Nanorods and Nanotubes in Aqueous Solution under an External Voltage