Abstract:Large-scale arrayed ZnO crystals with a series of novel morphologies, including tower-like, flower-like, and tube-like samples, have been successfully fabricated by a simple aqueous solution route. The morphology and orientation of the obtained ZnO crystal arrays can be conveniently tailored by changing the reactants and experimental conditions. For example, the tower-like ZnO crystal arrays were obtained in a reaction solution system including zinc salt, ammonia, ammonium salt, and thiourea, and the orientation of these tower-like crystals could be controlled by the contents of these reactants. Flower-like ZnO arrays were obtained at lower temperatures, and tube-like ZnO arrays were obtained by ultrasonic pretreatment of the reaction system. The growth mechanism of the tower-like and tube-like ZnO crystals was investigated by FESEM. The results show that tower-like crystals grow layer by layer, while tube-like crystals grow from active nanowires. Ultrasonic pretreatment is proved to be effective in promoting the formation of active nuclei, which have important effects on the formation of the tube-like ZnO crystals. In addition, large-scale arrays of these ZnO crystals can be successfully synthesized onto various substrates such as amorphous glass, crystalline quartz, and PET. This implies this chemical method has a wide application in the fabrication of nano-/microscale devices.

Fabrication and characterization of hexagonally patterned quasi-1D ZnO nanowire arrays

Conversion of large-scale oriented ZnO rod array into nanotube array under hydrothermal etching condition via one-step synthesis approach

Arrays of ZnO Nanowires Fabricated by a Simple Chemical Solution Route

Periodic ZnO Nanorod Arrays Defined by Polystyrene Microsphere Self-Assembled Monolayers

Fabrication of ZnO/Al2O3 core–shell nanostructures and crystalline Al2O3 nanotube

ZnO Nanowire and $\hbox{ws}_{2}$ Nanotube Electronics

Fabrication and characterization of single-crystalline ZnTe nanowire arrays

A General Approach For Fabricating Arc-Shaped Composite Nanowire Arrays By Pulsed Laser Deposition

Large Scale Fabrication Of Periodical Bowl-Like Micropatterns Of Single Crystal Zno

Growth mechanism and diameter control of well-aligned small-diameter ZnO nanowire arrays synthesized by a catalyst-free thermal evaporation method.

High-quality ZnO nanowire arrays directly fabricated from photoresists.

A New Method for Bulk-Quantity Synthesis of Patterned Well-Aligned Zno Nanowire Arrays

Inclined and ordered ZnO nanowire arrays developed on non-polar ZnO seed-layer films

Controllable Preparation of 1-D and Dendritic ZnO Nanowires and Their Large Area Field-Emission Properties

Fabrication of oriented ZnO nanorod arrays and their optical performances

Bio-inspired Fabrication of ZnO Nanorod Arrays and Their Optical and Photoresponse Properties

Controllable Synthesis of Ordered Zno Nanodots Arrays by Nanosphere Lithography

Wet Chemical Approaches to Patterned Arrays of Well-Aligned ZnO Nanopillars Assisted by Monolayer Colloidal Crystals

Large-scale fabrication of tower-like, flower-like, and tube-like ZnO arrays by a simple chemical solution route

Fabrication and Morphology of ZnO Nanorods Array Prepared from Aqueous Solution under an Assisted Electrical Field

Controllable growth and optical properties of ZnO nanostructures on Si nanowire arrays