Abstract:Large-scale arrayed ZnO crystals with a series of novel morphologies, including tower-like, flower-like, and tube-like samples, have been successfully fabricated by a simple aqueous solution route. The morphology and orientation of the obtained ZnO crystal arrays can be conveniently tailored by changing the reactants and experimental conditions. For example, the tower-like ZnO crystal arrays were obtained in a reaction solution system including zinc salt, ammonia, ammonium salt, and thiourea, and the orientation of these tower-like crystals could be controlled by the contents of these reactants. Flower-like ZnO arrays were obtained at lower temperatures, and tube-like ZnO arrays were obtained by ultrasonic pretreatment of the reaction system. The growth mechanism of the tower-like and tube-like ZnO crystals was investigated by FESEM. The results show that tower-like crystals grow layer by layer, while tube-like crystals grow from active nanowires. Ultrasonic pretreatment is proved to be effective in promoting the formation of active nuclei, which have important effects on the formation of the tube-like ZnO crystals. In addition, large-scale arrays of these ZnO crystals can be successfully synthesized onto various substrates such as amorphous glass, crystalline quartz, and PET. This implies this chemical method has a wide application in the fabrication of nano-/microscale devices.

A simple route to scalable fabrication of perfectly ordered ZnO nanorod arrays

Conversion of large-scale oriented ZnO rod array into nanotube array under hydrothermal etching condition via one-step synthesis approach

A large-scale-oriented ZnO rod array grown on a glass substrate via an in situ deposition method and its photoconductivity

A Simple Route to Controllable Growth of ZnOnanorod Arrays on Conducting Substrates

Arrays of ZnO Nanowires Fabricated by a Simple Chemical Solution Route

A Versatile Approach for the Synthesis of ZnO Nanorod-Based Hybrid Nanomaterials Via Layer-by-Layer Assembly

Periodic ZnO Nanorod Arrays Defined by Polystyrene Microsphere Self-Assembled Monolayers

Controllable Growth of Highly Ordered ZnO Nanorod Arrays Via Inverted Self-Assembled Monolayer Template.

Growth of Arrayed Nanorods and Nanowires of ZnO from Aqueous Solutions

Large-area zinc oxide nanorod arrays templated by nanoimprint lithography: control of morphologies and optical properties

Alignment-controlled Hydrothermal Growth of Well-Aligned ZnO Nanorod Arrays

Mechanical-Agitation-Assisted Growth of Large-Scale and Uniform ZnO Nanorod Arrays Within 3D Multichannel Monolithic Substrates

Large-scale fabrication of tower-like, flower-like, and tube-like ZnO arrays by a simple chemical solution route

Room-Temperature Surface-Erosion Route to Zno Nanorod Arrays and Urchin-Like Assemblies

Fabrication of ZnO/Al2O3 core–shell nanostructures and crystalline Al2O3 nanotube

Straight and Thin ZnO Nanorods: Hectogram-Scale Synthesis at Low Temperature and Cathodoluminescence.

Shape controllable synthesis of ZnO nanorod arrays via vapor phase growth

Fabrication of oriented ZnO nanorod arrays and their optical performances

A simple and novel route for the preparation of ZnO nanorods

ZnO Nanorod Arrays: Field-assisted Growth in Aqueous Solution and Field Emission Properties

Electrochemical Route to the Synthesis of Ultrathin ZnO Nanorod/nanobelt Arrays on Zinc Substrate