Abstract:Scalable and cost-effective synthesis and assembly of technologically important nanostructures in three-dimensional (3D) substrates hold keys to bridge the demonstrated nanotechnologies in academia with industrially relevant scalable manufacturing. In this work, using ZnO nanorod arrays as an example, a hydrothermal-based continuous flow synthesis (CFS) method is successfully used to integrate the nanoarrays in multi-channeled monolithic cordierite. Compared to the batch process, CFS enhances the average growth rate of nano-arrays by 125%, with the average length increasing from 2 mu m to 4.5 mu m within the same growth time of 4 hours. The precursor utilization efficiency of CFS is enhanced by 9 times compared to that of batch process by preserving the majority of precursors in recyclable solution. Computational fluid dynamic simulation suggests a steady-state solution flow and mass transport inside the channels of honeycomb substrates, giving rise to steady and consecutive growth of ZnO nano-arrays with an average length of 10 mu m in 12 h. The monolithic ZnO nano-array-integrated cordierite obtained through CFS shows enhanced low-temperature (200 degrees C) desulfurization capacity and recyclability in comparison to ZnO powder wash-coated cordierite. This can be attributed to exposed ZnO {10 (1) over bar0} planes, better dispersion and stronger interactions between sorbent and reactant in the ZnO nanorod arrays, as well as the sintering-resistance of nano-array configurations during sulfidation-regeneration cycles. With the demonstrated scalable synthesis and desulfurization performance of ZnO nano-arrays, a promising, industrially relevant integration strategy is provided to fabricate metal oxide nano-array-based monolithic devices for various environmental and energy applications.

Mechanical-Agitation-Assisted Growth of Large-Scale and Uniform ZnO Nanorod Arrays Within 3D Multichannel Monolithic Substrates

Conversion of large-scale oriented ZnO rod array into nanotube array under hydrothermal etching condition via one-step synthesis approach

Alignment-controlled Hydrothermal Growth of Well-Aligned ZnO Nanorod Arrays

Facile and Controllable Growth of ZnO 1D Nanostructure Arrays on Zn Substrate by Hydrothermal Process

Controllable Growth of Highly Ordered ZnO Nanorod Arrays Via Inverted Self-Assembled Monolayer Template.

ZnO Nanorod Arrays: Field-assisted Growth in Aqueous Solution and Field Emission Properties

Hydrothermal Synthesis of Well-Aligned ZnO Nanorod Arrays on Silicon

Scalable continuous flow synthesis of ZnO nanorod arrays in 3-D ceramic honeycomb substrates for low-temperature desulfurization

Growth of Arrayed ZnO Nanowires Using a Solution Method

Density-controlled Hydrothermal Growth of Well-Aligned ZnO Nanorod Arrays

4 Nm ZnO Nanocrystals Fabrication Through Electron Beam Irradiation on the Surface of a ZnO Nanoneedle Formed by Thermal Annealing

Preparation of ZnO Nanorod Arrays by Seed-assisted Chemical Bath Deposition Method

A simple route to scalable fabrication of perfectly ordered ZnO nanorod arrays

Large-area zinc oxide nanorod arrays templated by nanoimprint lithography: control of morphologies and optical properties

Growth of Arrayed Nanorods and Nanowires of ZnO from Aqueous Solutions

Large-scale fabrication of tower-like, flower-like, and tube-like ZnO arrays by a simple chemical solution route

A Simple Route to Controllable Growth of ZnOnanorod Arrays on Conducting Substrates

Architecting three-dimensional ZnO nanorods

Ordered Growth and Photoluminescence of ZnO Nano-Arrays on Silicon Substrates with Seed Film by Hydrothermal Method

Large Scale Fabrication Of Periodical Bowl-Like Micropatterns Of Single Crystal Zno

Patterned Growth of ZnO Nanorod Arrays on a Large-Area Stainless Steel Grid.