Abstract:Highly tetrahedral amorphous carbon (ta-C) films and its hydrogenated form (ta-C:H) have been deposited using a filtered cathodic are. In this paper, the optical and electronic band-gaps of amorphous diamond and its hydrogenated form ta-C:H, are shown to be in the range 2 eV. The H content of ta-C: H is found to be about 3 at.% using elastic recoil detection analysis (ERDA) and electron energy loss spectroscopy (EELS) is used to show that ta-C:H does keep its tetrahedral structure. Both materials are found to be stable at temperatures up to 1000K. The room temperature conductivity of 10(-7)10(-8)Omega(-1)cm(-1) is shown to be thermally activated, with activation energies in the range 0.2-0.3 eV. A detailed study made from the current-voltage characteristics of ta-Clp-Si heterojunctions shows that current flow is space-charge limited (SCLC) and influenced by bulk traps. The density of states profile, N(E), in the region of the quasi-Fermi level is calculated using the differential method and found to be of the order 10(18) cm(-3) eV(-1). Optical absorption data is coupled with the electrical results to confirm that the valence band density of states is of the order 10(21) cm(-3) eV(-1). It is also shown that there is a reduction of nearly one order of magnitude in the N(E) at the quasi-Fermi level upon hydrogenation. SCLC measurements are complemented with surface admittance measurements (SAM) which yield a value of 10(11) cm(-2) eV(-1) for the interfacial density of states at the ta-C/p-Si junction. A decrease in N-ss is also observed at the ta-C:H/p-Si interface in agreement with the SCLC results.

N-Type Doping of Highly Tetrahedral Diamond-Like Amorphous Carbon

Doping Of Highly Tetrahedral Amorphous-Carbon

Tetrahedral Amorphous-Carbon Properties and Applications

Electronic Properties of Tetrahedral Amorphous Carbon (Ta-C) Films Containing Nanotube Regions

Substitutional Nitrogen Doping of Tetrahedral Amorphous Carbon

Structural Characteristics and Electrode Activities of Phosphorus Incorporated Tetrahedral Amorphous Carbon Films

Electronic density of states in highly tetrahedral amorphous carbon

The Structure of Boron-, Phosphorus- and Nitrogen-Doped Tetrahedral Amorphous Carbon Deposited by Cathodic Arc

Photoconductivity in Highly Tetrahedral Diamondlike Amorphous Carbon

Influence of Carbon Ion Energy on Properties of Highly Tetrahedral Diamond-Like Carbon

Influence of Ion Energy and Substrate Temperature on the Optical and Electronic Properties of Tetrahedral Amorphous Carbon (Ta-C) Films

Electronic-Properties of Semiconducting Diamond-Like Carbon Diamond

Gap States, Doping And Bonding In Tetrahedral Amorphous-Carbon

Influence of Phosphorus Doping Level and Acid Pretreatment on the Voltammetric Behavior of Phosphorus Incorporated Tetrahedral Amorphous Carbon Film Electrodes

Structural and Electrical Characterization of Highly Tetrahedral-Coordinated Diamond-Like Carbon Films Grown by Pulsed-Laser Deposition

Properties of N-Type Tetrahedral Amorphous Carbon (Ta-C)/p-type Crystalline Silicon Heterojunction Diodes

Seebeck Measurements of N-Doped Diamond Thin Film

Effect of Phosphorus Content on Structural Properties of Phosphorus Incorporated Tetrahedral Amorphous Carbon Films

Photoresponse Characteristics of N-Type Tetrahedral Amorphous-Carbon P-Type Si Heterojunction Diodes

Doping of rf plasma deposited diamond-like carbon films

Properties of Tetrahedral Amorphous Carbon Prepared by Vacuum Arc Deposition