Synthesis, structure, and characterization of new low-firing microwave dielectric ceramics: (Ca1-3xBi2x Phi(x))MoO4

Jing Guo,Clive A. Randall,Gaoqun Zhang,Di Zhou,Yuyan Chen,Hong Wang

DOI: https://doi.org/10.1039/c4tc00698d

IF: 6.4

2014-01-01

Journal of Materials Chemistry C

Abstract:A series of A-site deficient scheelite ceramics (Ca1-3xBi2x Phi(x))MoO4 (x = 0.005, 0.015, 0.025, 0.035, 0.05, 0.1, 0.15, and 0.2, and Phi: A-site vacancy) were synthesized via the solid state reaction route. The structures were analyzed using a combination of X-ray diffraction and X-ray absorption fine structure spectroscopy (Mo K-edge and Bi L-3-edge) to determine average and local structures. A series of defective scheelite (Ca1-3xBi2x Phi(x))MoO4 compositions can be formed as a solid solution, and local structures of Mo and Bi indicate that a MoO4 tetrahedron and a BiO8 polyhedron become more distorted with the x value. The large change in the Bi-O1 (the first shell) and Bi-O2 (the second shell) distances is an important insight into the nature of the defective structures. The statistical disorder of a Bi-O bond is one order of magnitude larger than that of a Mo-O bond. The microstructures and microwave dielectric properties were investigated by scanning electron microscopy and through network analyzer resonance studies. All the compositions can be sintered well below 900 degrees C. With slight Bi substitutions (x = 0.005 and 0.015), the samples exhibit improved Q x f values. At x = 0.15, temperature stable (TCF = -1.2 ppm per degrees C) low-firing (ST = 700 degrees C) microwave dielectric materials were obtained with a permittivity of 21.2 and a Q x f value of 29 300 GHz. The factors affecting dielectric properties are associated with the local structures of Mo and Bi across the solid solution.