Abstract:In the present work, the xBi(Fe1/3Mo2/3)O-4-(1-x)BiVO4 (0.0 <= x <= 1.0) ceramics were prepared via the solid state reaction method. All the ceramics can be densified at low sintering temperatures around 820 degrees C. At room temperature, the BiVO4 type scheelite monoclinic solid solution was formed in ceramic samples with a composition of x <= 0.10. When x lies between 0.1 and 0.7, a BiVO4 scheelite tetragonal phase is formed at room temperature. In the range 0.7 <= x < 0.9, the ceramic samples were found to be composites consisting of BiVO4 type tetragonal and Bi(Fe1/3Mo2/3)O-4 type monoclinic scheelite phases, and when x >= 0.9, the Bi(Fe1/3Mo2/3)O-4 type monoclinic scheelite solid solution was formed. In the BiVO4 type monoclinic solid solution region, the phase transition to tetragonal phase was studied by in situ Raman and Far-Infrared spectroscopies and by thermal expansion analysis. All of these methods indicated that the phase transition temperature almost linearly decreased from 255 degrees C for pure BiVO4 to about -9 degrees C for x = 0.1 sample. High performance microwave dielectric properties with a high permittivity of about 74.8, high Qf values above 11 500 GHz, and a small temperature coefficient of resonant frequency within +20 ppm per degrees C in a wide temperature range of 20-140 degrees C can be obtained in the composite ceramic sample with 60 mol% x = 0.10 composition and 40 mol% x = 0.02 composition. The xBi(Fe1/3Mo2/3)O-4-(1-x)BiVO4 (0.0 <= x <= 1.0) ceramics might provide useful candidate materials for microwave integrated capacitive devices, such as filters, antennas, etc.

Sintering Characteristics, Phase Transitions, and Microwave Dielectric Properties of Low-Firing [(na 0.5bi 0.5) X Bi 1− X ](W X V 1− X )O 4 Solid Solution Ceramics

Sintering characteristics, phase transitions, and microwave dielectric properties of low-firing [(Na<sub>0.5</sub>Bi<sub>0.5</sub>)xBi<sub>1-x</sub>](W<sub>x</sub>V<sub >1-x</sub>)O<sub>4</sub> solid solution ceramics

Phase evolution, phase transition, and microwave dielectric properties of scheelite structured xBi(Fe 1/3Mo 2/3)O 4-(1-x) BiVO 4 (0.0 ≤ x ≤ 1.0) low temperature firing ceramics

Crystal Structure and Microwave Dielectric Behaviors of Scheelite Structured (1-X)bivo4-xla2/3moo4 (0.0 ≤ X ≤ 1.0) Ceramics with Ultra-Low Sintering Temperature

Structure-property relationships of low sintering temperature scheelite-structured (1 -x)BiVO4-xLaNbO4 microwave dielectric ceramics

Sintering behavior, phase evolution and microwave dielectric properties of Bi{Sb1-x(Nb0.992V0.008)x}O4 ceramics

Influence of W substitution on crystal structure, phase evolution and microwave dielectric properties of (Na0.5Bi0.5)MoO4 ceramics with low sintering temperature

Phase evolution and microwave dielectric properties of xBi(2/3)MoO₄-(1 -x)BiVO₄ (0.0 ≤ x ≤ 1.0) low temperature firing ceramics.

Crystal Structure And Microwave Dielectric Behaviors Of Ultra-Low-Temperature Fired X(Ag0.5bi0.5)Moo4-(1-X)Bivo4 (0.0 <= X <= 1.0) Solid Solution With Scheelite Structure

Phase Transition, Raman Spectra, Infrared Spectra, Band Gap And Microwave Dielectric Properties Of Low Temperature Firing (Na0.5xbi1-0.5x)(Moxv1-X)O-4 Solid Solution Ceramics With Scheelite Structures

Phase Evolution, Phase Transition, Raman Spectra, Infrared Spectra, And Microwave Dielectric Properties Of Low Temperature Firing (K0.5xbi1-0.5x)(Moxv1-X)O-4 Ceramics With Scheelite Related Structure

Phase evolution and microwave dielectric properties of (Li 0.5Bi0.5)(W1-xMox)O4 (0.0 ≤ x ≤ 1.0) ceramics with ultra-low sintering temperatures

Ultra‐Low Firing High‐k Scheelite Structures Based on [(li0.5bi0.5)xbi1−x][moxv1−x]o4 Microwave Dielectric Ceramics

Nonstoichiometric microwave dielectric ceramics [(Na0.5-xBi0.5+x/3)0.5Ca0.5]MoO4 with low sintering temperatures

(Nabi)0.5moo4–bipo4 Microwave Dielectric Ceramics with Ultra-Low Sintering Temperatures

Low Sintering Temperature, Temperature-Stable Scheelite Structured Bi[V1−x (fe1/3w 2/3)x]o4 Microwave Dielectric Ceramics

Low-Firing Ba_4(Nd_(0.85)Bi_(0.15))_(28/3)Ti_(18)O_(54) Microwave Ceramics

Novel Scheelite‐type [ca0.55(nd1‐xbix)0.3]moo4 (0.2 ≤ X ≤ 0.95) Microwave Dielectric Ceramics with Low Sintering Temperature

Microwave Dielectric Properties of Low Firing Temperature Stable Scheelite Structured (Ca,bi)(mo,v)o-4 Solid Solution Ceramics for LTCC Applications

Structure, Phase Evolution, And Microwave Dielectric Properties Of (Ag0.5bi0.5)(Mo0.5w0.5)O-4 Ceramic With Ultra Low Sintering Temperature

Synthesis, structure, and characterization of new low-firing microwave dielectric ceramics: (Ca1-3xBi2x Phi(x))MoO4