Crystal Structure And Microwave Dielectric Behaviors Of Ultra-Low-Temperature Fired X(Ag0.5bi0.5)Moo4-(1-X)Bivo4 (0.0 <= X <= 1.0) Solid Solution With Scheelite Structure

Di Zhou,Li-Xia Pang,Ze-Ming Qi

DOI: https://doi.org/10.1021/ic501306n

IF: 4.6

2014-01-01

Inorganic Chemistry

Abstract:x(Ag0.5Bi0.5)MoO4-(1 - x)BiVO4 (0.0 <= x <= 1.0) ceramics were prepared by using the solid-state reaction technique. Ceramics with x < 0.10 had a monoclinic scheelite structure, while those with >= 0.10 were tetragonal scheelite solid solutions. This indicates that the phase transformation temperature of BiVO4 was lowered through the formation of a solid solution. The thermal expansion data of the x = 0.08 sample showed that the thermal expansion coefficient was increased suddenly from +8 to +15 ppm/ degrees C at about 60.6 degrees C due to the phase transition. Similarly, a maximum value of microwave dielectric permittivity was revealed at about 65 degrees C for the x = 0.08 sample. All of the ceramics could be well sintered below 700 degrees C. Good microwave dielectric behaviors, with relative permittivity > 75 and Q(f) > 9000 GHz, were obtained in ceramics with compositions near x = 0.10. Both the THz data and the infrared spectra were used to study the intrinsic dielectric behavior of the materials at microwave frequencies.