Crystal Structure and Microwave Dielectric Behaviors of Scheelite Structured (1-X)bivo4-xla2/3moo4 (0.0 ≤ X ≤ 1.0) Ceramics with Ultra-Low Sintering Temperature

Li-Xia Pang,Di Zhou,Wei-Guo Liu,Ze-Ming Qi,Zhen-Xing Yue

DOI: https://doi.org/10.1016/j.jeurceramsoc.2017.10.051

IF: 5.7

2017-01-01

Journal of the European Ceramic Society

Abstract:In the present work, a novel (1-x)BiVO4-xLa2/3MoO4 scheelite related solid solution ceramics were prepared via solid state reaction method. As revealed by X-ray diffraction data, the crystal structure changed continuously from monoclinic to tetragonal phase at x=0.10 and then the tetragonal solid solution was kept in a wide composition range up to x=0.70. Both the Raman and far infrared spectra supported this phenomenon. When x value reached 0.9, the ceramic sample was found to composed of both scheelite tetragonal and monoclinic La2/3MoO4 phases. Large microwave permittivity value between 68±0.2–73±0.3 can be achieved in compositions with 0.02≤x≤0.10 with high Qf value about 10,000±500GHz. This series of solid solution ceramics might be candidate for both dielectric resonator and low temperature co-fired ceramic technology.