Abstract:This study utilized a conventional solid-state reaction method to prepare ZnO–Bi 2 O 3 –Sb 2 O 3 –Co 3 O 4 –Mn 3 O 4 –Nb 2 O 5 varistors sintered at low temperatures of 860 °C–880 °C. The effects of the different amounts of SiO 2 and SiO 2 -B 2 O 3 co-doping on the microstructure and varistor properties were investigated. The nonlinearity coefficient (α) increased from 51 for the sample without adding SiO 2 to 66 for the sample with 1.0wt% SiO 2 , and the breakdown voltage increased from 834 to 1260 V/mm. However, with excess SiO 2 addition, the α value gradually decreased from 66 for the sample with 1 wt% SiO 2 to 52 for the sample with 2.0 wt% SiO 2 , while the breakdown voltage continued to increase. Co-doping SiO 2 –B 2 O 3 improves liquid phase sintering due to the relatively low melting point of SiO 2 –B 2 O 3 –Bi 2 O 3 additives. The α value increased from 66 for the sample without adding B 2 O 3 to 83 for the sample with 2.0 wt% B 2 O 3 , while the breakdown voltage decreased from 1260 to 1120 V/mm. In comparison to higher temperature alternatives, the lower sintering temperatures (860 °C–880 °C) used in this study result in lower energy consumption during the manufacturing process. Because of their favorable cost-energy efficiency ratio, the SiO 2 –B 2 O 3 co-doped ZnO–Bi 2 O 3 varistors emerge as promising candidates for large-scale production.

Low Temperature Sintering of Doped ZnO-V2O5 Varistors

Low-temperature sintering of high voltage gradient ZnO-based thick film varistors

LOW-TEMPERATURE SINTERING OF ZINC OXIDE-BASED VARISTORS PREPARED BY A HIGH-ENERGY BALL MILL

Effects of SiO2 and B2O3 on electrical properties of low-temperature sintered ZnO–Bi2O3 varistors

Effect of the Sintering Temperature on the Electrical Properties of Y-Al-doped ZnO Varistors

Electrical Properties of ZnO-Borosilicate Glass Varistors Prepared with the Method of One Step

An ultralow concentration of Cr2O3 dopants driven lower temperature sintering ZnO‐based varistor ceramics

Effect of B2O3 doping on the microstructure and electrical properties of ZnO-based varistors

Influence of Dopants on Electrical Properties of ZnO-V 2 O 5 Varistors Deduced from AC Impedance and Variable-Temperature Dielectric Spectroscopy

Admittance Spectroscopy of Y<sub>2</sub>O<sub>3</sub>-Doped ZnO Varistors Sintered at Different Temperature

Preparation of Ultrahigh Potential Gradient of ZnO Varistors by Rare-Earth Doping and Low-Temperature Sintering

Microstructure and electrical properties of Pr 6 O 11 doped ZnO-Bi 2 O 3 -based varistors

Optimization of Sintering Temperature and Doping Level of Cr2O3 in ZnO-Pr6O11-Based Varistor Ceramics

Preparation of High Potential Gradient ZnO-Based Thick-Film Varistors by High-Energy Ball Milling and Low-temperature Sintering

Microstructure design and optimization of ZnO-Bi 2O 3-Sb 2O 3 based ceramic varistors

Structural and electrical properties of ZnO–V2O5–TiO2–Co2O3–MnO varistor ceramics with low sintering temperature

B 2O 3-doped ZnO-Pr 6O 11 based varistor ceramics

High Potential Gradient of Zno Varistors Prepared by Y2o3-Doping and Low-Temperature Sintering

Elaboration and electrical characterization of ZnO-based varistor ceramics in different sintering temperatures

Influence of ZnSb2O6 Doping on Phase, Electrical and Dielectric Properties of ZnO Varistors