Abstract:The effect of Bi2O3 on ZnO-based varistor ceramic sintered around 800 °C is still not fully understood, because most of the ceramic cannot reach full densification at this low-temperature. Therefore, (balanced) ZnO–0.5 mol% V2O5–0.5 mol% MnCO3–0.5 mol% Co2O3–0.5 mol% TiO2–xmol% Bi2O3 (x = 0, 0.01, 0.05, 0.1 and 0.2) ceramic was designed and prepared by the solid-state sintering at 800 °C. The effect of Bi2O3 variation on the microstructure and electrical nonlinearity of the sample material was studied by using methods of XRD SEM, STEM, EDS and E–J test. Bi2O3 can further activate the reaction at the interface between the V-rich liquid phase and ZnO grains during sintering. This enhanced interface reaction is the key reason to the extremely low-temperature sintering of the ceramic at 800 °C. The variation of Bi2O3 in the 0–0.2 mol% range barely influences the constituents of the ceramic, which consists of ZnO main phase and two other secondary phases: Zn3(VO4)2 and Zn2TiO4. Most of Bi2O3 tends to segregate at grain boundaries. As a result, a soaking time longer than 4 h is needed to allow Bi ions diffusing into enough grain boundaries and improving the nonlinearity of ZnO based varistor ceramic. The sample containing 0.01 mol% Bi2O3 and sintered at 800 °C for 8 h has the best properties of a 43.3 nonlinear coefficient, a 2300 V/mm breakdown voltage and a 0.13 mA/cm2 leakage current density.

LOW-TEMPERATURE SINTERING OF ZINC OXIDE-BASED VARISTORS PREPARED BY A HIGH-ENERGY BALL MILL

Elaboration and electrical characterization of ZnO-based varistor ceramics in different sintering temperatures

Structural and electrical properties of ZnO–V2O5–TiO2–Co2O3–MnO varistor ceramics with low sintering temperature

An ultralow concentration of Cr2O3 dopants driven lower temperature sintering ZnO‐based varistor ceramics

Microstructure design and optimization of ZnO-Bi 2O 3-Sb 2O 3 based ceramic varistors

Effects of SiO2 and B2O3 on electrical properties of low-temperature sintered ZnO–Bi2O3 varistors

Microstructure Design and Optimization of ZnO-Bi2O3-Sb2O3 Based Ceramic Varistors

Reliability enhancement of zinc oxide varistors using sputtered silver electrodes.

Excellent Electrical Properties of Zinc-Oxide Varistors by Tailoring Sintering Process for Optimizing Line-Arrester Configuration

The Dependence of Sintering Temperature on Schottky Barrier and Bulk Electron Traps of ZnO Varistors

Microstructure and Electrical Properties of Ga2o3 Doping on Zno Varistor Ceramics with Different Sintering Temperature

High‐performance ZnO varistor ceramics prepared by arc‐induced flash sintering with low energy consumption at room temperature

Optimization of Sintering Temperature and Doping Level of Cr2O3 in ZnO-Pr6O11-Based Varistor Ceramics

Effect of Bi2O3 on the ZnVMnCoTiO based varistor ceramic sintered at 800 °C

Improving Age Stability and Energy Absorption Capabilities of Zno Varistors Ceramics

High voltage gradient zinc oxide varistors for line surge arresters and GIS tank-type arresters

Properties of ZnO Varistors Prepared with Nano-Sized Powders

Admittance Spectroscopy of Y<sub>2</sub>O<sub>3</sub>-Doped ZnO Varistors Sintered at Different Temperature

Effects of raw particle size and annealing on microstructure, electrical and mechanical behaviors of ZnO-based varistors

Impact of calcination on low-temperature sintered Bi2O3 varistors: Varistor properties and surge current absorption

The Effect of ZnO Powder Particle Distribution on Performance of Multilayer Chip Varistor