Abstract:In this paper, the effect of the raw particle size and the annealing process on the compositions, microstructure, mechanical, thermal, and electrical properties of ZnO varistors was investigated using X-ray diffraction, infrared, X-ray photoelectron spectroscopy, scanning electron microscopy, electric field–current density, capacitance–voltage, mechanical, and thermal expansion measurements. Furthermore, the ZnO grain growth mechanism during the annealing process was discussed in detail. Results show that when the raw particle size equaled 90 nm and sintering was performed at 1100 °C for 2 h, the obtained ZnO-based varistors possessed excellent mechanical, thermal, and electrical properties; the E1mA, α, JL, and K values were 1015.3 V mm–1, 37.98, 2.45 μA cm–2, and 1.37, respectively, due to the highest bulk density and the finest uniform particle size distribution. When annealing occurred at 300 °C for three times, values of σf, KIC, E1mA, α, JL, and K reached 175.35 MPa, 1.96 MPa m1/2, 1180.2 V mm–1, 43.58, 2.15 μA cm–2, and 1.2, indicating improvements of approximately 14.7%, 4%, 16.2%, 14.7%, − 12.2%, and 11.11% compared with those of the non-annealed ZnO-based varistors, respectively, being due to the improved uniformity of grain size distribution and the re-distribution of donor Al3+ and Y3+ in the ZnO crystal and grain boundary. The annealing process lead to the transformation of Sb3+ to Sb5+ in the ZnO crystal, which could generate two additional coordination sites. The newly generated sites could combine with O2- in other crystals to increase the grain growth, resulting in clear grain growth on the surface, improved grain size distribution, and regular grain shape in the interior of ZnO-based varistors.

Properties of ZnO Varistors Prepared with Nano-Sized Powders

Characterisation of Zno-Based Varistors Prepared from Nanometre Precursor Powders

Reliability enhancement of zinc oxide varistors using sputtered silver electrodes.

High voltage gradient zinc oxide varistors for line surge arresters and GIS tank-type arresters

Excellent Electrical Properties of Zinc-Oxide Varistors by Tailoring Sintering Process for Optimizing Line-Arrester Configuration

High Voltage Gradient ZnO Nonlinear Resistor Doped with Rare-Earth Oxide

Microstructural analysis of varistors prepared from nanosize ZnO

Simultaneously Enhanced Potential Gradient and Nonlinearity of ZnO Varistor Ceramics by MnO Doping with Nano-Sized ZnO Powders

Effects of raw particle size and annealing on microstructure, electrical and mechanical behaviors of ZnO-based varistors

Study on Composition of ZnO Varistor Added with Rare-Earth Oxide to Improve its Electrical Performance

Residual Voltage Properties of ZnO Varistors Doped with Y2O3 for High Voltage Gradient

ZnO Varistors with High Voltage Gradient and Low Leakage Current by Doping Rare-Earth Oxide

Fabrication of High Performance Multilayer Zno Varistors with Chemically Synthesized Doped Zinc Oxide Powder

Influence of ZnSb2O6 Doping on Phase, Electrical and Dielectric Properties of ZnO Varistors

Effect of B2O3 Doping on the Microstructure and Electrical Properties of ZnO-Based Varistors

Influence of Rare-Earth Oxide Additives on Electrical Performance of ZnO Varistor

Elaboration and electrical characterization of ZnO-based varistor ceramics in different sintering temperatures

Improving Age Stability and Energy Absorption Capabilities of Zno Varistors Ceramics

Comprehensive Performances of ZnO Varistors Tailored by Multi-elements Doping

Effect of Sc2O3 doping on microstructure and electrical properties of ZnO–Bi2O3-based varistors