Elaboration and electrical characterization of ZnO-based varistor ceramics in different sintering temperatures

Faiçal Kharchouche,Samia Latreche

DOI: https://doi.org/10.1007/s10854-024-12602-8

2024-04-25

Journal of Materials Science Materials in Electronics

Abstract:The method applied in this study to develop conventional sintered varistors is based on liquid synthesis, The percentage of raw materials used is as follows: 98 mol% ZnO, 0.5 mol% Bi 2 O 3 , 0.5 mol% Sb 2 O 3 , 0.5 mol% Co 2 O 3 , 0.5 mol% MnO 2 was sintered in a sintering temperature cycle from 900 to 1200 °C with different sintering times up to 120 min, the highest densification rates, 98.56%, are obtained at the temperature of 1200 °C, the grain sizes are greater than 1.61 μm for the temperature of 900 °C and increase little from one sample to another for all sintering temperatures. The presence of a spinel phase Zn 7 Sb 2 O 12 as well as Bi 2 O 3 . The nonlinearity coefficient was high for the majority of sintered varistors at temperatures of 1000 °C and 1100 °C such that α > 35. The trigger field values ( E a) are nearly identical for all sintering temperatures, The electric fields for sintering at 1000 °C are a little high at about 373 V.mm −1 as a maximum value, 263 V.mm −1 for sintering at 1100 °C and 258 V. mm −1 for sintering at 1200 °C and we can also note that the density value of the leakage current is very low.

engineering, electrical & electronic,materials science, multidisciplinary,physics, condensed matter, applied