Effect of Bi2O3 on the ZnVMnCoTiO based varistor ceramic sintered at 800 °C

Ming Zhao,Wen-zheng Cui,Zhuo-cheng Liu,Hua Chen

DOI: https://doi.org/10.1007/s10854-021-06496-z

2021-07-01

Abstract:<p class="a-plus-plus">The effect of Bi<sub class="a-plus-plus">2</sub>O<sub class="a-plus-plus">3</sub> on ZnO-based varistor ceramic sintered around 800 °C is still not fully understood, because most of the ceramic cannot reach full densification at this low-temperature. Therefore, (balanced) ZnO–0.5 mol% V<sub class="a-plus-plus">2</sub>O<sub class="a-plus-plus">5</sub>–0.5 mol% MnCO<sub class="a-plus-plus">3</sub>–0.5 mol% Co<sub class="a-plus-plus">2</sub>O<sub class="a-plus-plus">3</sub>–0.5 mol% TiO<sub class="a-plus-plus">2</sub>–<em class="a-plus-plus">x</em>mol% Bi<sub class="a-plus-plus">2</sub>O<sub class="a-plus-plus">3</sub> (<em class="a-plus-plus">x</em> = 0, 0.01, 0.05, 0.1 and 0.2) ceramic was designed and prepared by the solid-state sintering at 800 °C. The effect of Bi<sub class="a-plus-plus">2</sub>O<sub class="a-plus-plus">3</sub> variation on the microstructure and electrical nonlinearity of the sample material was studied by using methods of XRD SEM, STEM, EDS and <em class="a-plus-plus">E–</em><em class="a-plus-plus">J</em> test. Bi<sub class="a-plus-plus">2</sub>O<sub class="a-plus-plus">3</sub> can further activate the reaction at the interface between the V-rich liquid phase and ZnO grains during sintering. This enhanced interface reaction is the key reason to the extremely low-temperature sintering of the ceramic at 800 °C. The variation of Bi<sub class="a-plus-plus">2</sub>O<sub class="a-plus-plus">3</sub> in the 0–0.2 mol% range barely influences the constituents of the ceramic, which consists of ZnO main phase and two other secondary phases: Zn<sub class="a-plus-plus">3</sub>(VO<sub class="a-plus-plus">4</sub>)<sub class="a-plus-plus">2</sub> and Zn<sub class="a-plus-plus">2</sub>TiO<sub class="a-plus-plus">4</sub>. Most of Bi<sub class="a-plus-plus">2</sub>O<sub class="a-plus-plus">3</sub> tends to segregate at grain boundaries. As a result, a soaking time longer than 4 h is needed to allow Bi ions diffusing into enough grain boundaries and improving the nonlinearity of ZnO based varistor ceramic. The sample containing 0.01 mol% Bi<sub class="a-plus-plus">2</sub>O<sub class="a-plus-plus">3</sub> and sintered at 800 °C for 8 h has the best properties of a 43.3 nonlinear coefficient, a 2300 V/mm breakdown voltage and a 0.13 mA/cm<sup class="a-plus-plus">2</sup> leakage current density.</p>

engineering, electrical & electronic,materials science, multidisciplinary,physics, condensed matter, applied