Abstract:In this study, a high valued product submicronic ?-alumina was successfully extracted from aluminum slags generated by the local aluminum industry. The extraction technique was based on the leaching of slags by H2SO4 followed by precipitation. The coarser aluminum-rich fractions of the slags were used in this study instead of the finer oxide-rich fractions that were commonly used in previous studies. The precipitation of the leached slags by NH4OH was controlled by a zetameter in order to determine the optimal precipitation pH. Then, the obtained gel showing the higher precipitation rate and the finer particle size was calcined at 1200 ?C and characterized by the XRF, XRD, FTIR, SEM, EDS, and laser granulometry. Even without any pretreatment of slags, the XRF analysis revealed that a high purity and high extraction efficiency of 99.2% and 93.75% respectively could be achieved just at a leaching acid concentration of 15%. The XRD spectrum shows that the produced alumina was pure a-corundum, which was confirmed by the FTIR spectrum showing only the Al-O bonds. The laser granulometry showed that the recovered powder exhibited a wide particle size distribution, which was between 50 nm and 20 ?m, while the average particle size (d50) was about 400 nm. The SEM observations revealed that the grains were in the form of submicronic whiskers. The above characteristics allowed the obtained alumina powder in this study to be used in the usual applications of alumina such as refractory, ceramic fibers, abrasive, etc. The obtained powders may also assume applications as a thermally stable substitute for the commonly used transition alumina powders, which needs further investigations in future studies.

Synthesis of ultrafine alpha-alumina powder by pyrolysis of ammonium aluminium carbonate hydroxide

Production of ultrafine alpha alumina powders and fabrication of fine grained strong ceramics

Synthesis and sintering behavior of a nanocrystalline α-alumina powder

Synthesis of Nano-Alumina Hydroxide Sol Using Sol-gel Method

Synthesis of nano α-alumina powders using hydrothermal and precipitation routes: a comparative study

EFFECT OF NH4HCO3 ON PORE STRUCTURE OF ALUMINA

Synthesis and phase formation mechanism of alpha-Fe2O3 powders by hydrothermal reaction method

Synthesis of α-Al2O3 Nanopowders at Low Temperature from Aluminum Formate by Combustion Process

Facile synthesis of nano-crystalline alpha-alumina at low temperature via an absolute ethanol sol-gel strategy

Self-propagating high-temperature synthesis and reaction mechanism of super-fine particles of gamma-LiAlO2

Synthesis of submicronic α-alumina from local aluminum slags

Preparation And Characterization Of Gamma-Al2o3 By Polyaluminum Chloride With High Al-13 Content

Lowering the synthesis temperature of α‐Al2O3 by increasing the content of pentacoordinate aluminum in the precursors

Study on Preparation and Characterization of gamma-Al(2)O(3) from Coal Fly Ash

Synthesis of NdAlO3 Fine Ceramic Powders Via Co-precipitation Process

Self-propagating High-temperature Synthesis and Reaction Mechanism of Super-fine Particles of γ-LiAlO2

Synthesis and structural characterization of alumina nanoparticles

Preparation and characterisation of boehmite precursor and sinterable alumina powder from aqueous aluminium chloride-urea reaction

Preparation of α-Al2O3 by low-temperature calcining γ-Al2O3 with α-phase seed in-situ obtained by ball milling

Study on ultrasound-assisted preparation of sphere-like high-purity alumina

Some properties of aluminium-nitride powder prepared by metal-organic chemical vapour deposition