Abstract:In the present paper, homogenous precipitation with Nd(NO)3.6H2O and (NH)2CzO4.2H2O, a strong base anion exchange resin and strong acidic cation exchange resin, respectively, and subsequent calcination of precursors at 700 C were used to synthesize Nd2O3 nanoparticles. In the precipitation from homogeneous solution, the relative supersaturation is always low and the local reagent excesses do not occur because the precipitating agent appears homogeneously throughout the entire solution. In general, homogeneous precipitates are better suited for analysis than precipitates formed by direct addition of a reagent. The concentration of reactant, reaction temperature and time are important factors which dominate the morphology and structure size of the Nd2O3 nanoparticles. Assay results showed that between 40 and 50 degrees C, when the ion exchange resin was added tardily with continuous stirring and mixing, the precursor could be obtained after being filtered, washed, and dried at 80 degrees C. The Nd2O3 Sample was obtained via calcination of the precursor at 700 degrees C for 1.5 h. The morphology, size and distribution of the precursors and samples were characterized by TG-DTA, XRD, TEM, HR-TEM, SAED and BET techniques. The forming mechanism of homogenous precipitation was discussed detailedly. The results indicated that the Nd2O3 nanocrystal prepared with the present method belonged to hexagonal crystal system, and its average diameter was 26-32 nm with better decentralization. The electron diffraction pattern which had a clear and regular lattice of Nd2O3 confirmed that the particles were monocrystals. The specific surface area of sample a and sample b was 42. 57 and 29.43 m2 x g(-1), respectively. The ion exchange resin homogenous precipitation method has such advantages as low cost, environmentally benign innocuity of the starting reagents, the simplicity of the synthetic route, easy recycling of ion exchange resin and so on, making it a promising method to be scaled up for industrial production.

Synthesis of NdAlO3 Fine Ceramic Powders Via Co-precipitation Process

Synthesis of SrLaAlO 4 Fine Ceramic Powders by Co-Precipitation Process

Synthesizing nano LaAlO3 powders via co-precipitation method

Influence of Ammonium Chloride on Preparation of Α-Al2o3 Nanopowder by Thermal Decomposition of Ammonium Aluminum Carbonate Hydroxide

Preparation of Nd: YAG Ceramic by Co-precipitation Reaction via Normal-strike

Preparation of Ultrafine Α-Al2o3 Powder by Homogenous Precipitation

Study on the Morphology of Α-Al2o3 Precursor Prepared by Precipitation Method

Preparation of Ultrafine Α-Al2o3 Powders by Catalytic Sintering of Ammonium Aluminum Carbonate Hydroxide at Low Temperature

Preparation of NiAl2O4/Al2O3 composite nanopowder

Effects of Different Aluminum Sources and Calcination Temperatures on the Synthesis of Ultrafine Aln Powder Via Carbothermal Reduction Nitridation

Synthesis and sintering behavior of a nanocrystalline α-alumina powder

Preparation of Nd2O3 Nanoparticles by Ion Exchange Resin Homogenous Precipitation Method

Synthesis of Nanostructured Nd:Y2o3 Powders by Carbonate-Precipitation Process for Nd:Yag Ceramics

Effects of Al2o3 Phase Composition on Alon Powder Synthesis Via Aluminothermic Reduction and Nitridation

Influence of Synthesis Temperature on the ZnNb2O6 Powders Prepared Via Co-Precipitation Method

Preparation and Characterization of Y3Al5O12:Nd Phosphor Powders by Ultrasonic Atomization and Co-precipitation Process

Novel Way to Synthesize Nanocrystalline Aluminum Nitride from Coarse Aluminum Powder

PREPARE ULTRAFINE α-Al2O3 POWDER BY PRECIPITATION METHOD

Preparation, sintering behavior and microstructure of Al2O3-Coated Ni powders

Synthesis of Γ -Al 2 O 3 Nanoparticles by Chemical Precipitation Method

Influence of Solution Concentration on the Ceramic Performance of ZnNb2O6 Powders Prepared by Co-precipitation Method