Abstract:The processes of cathodic reduction of U(III) ions to metal in a low–melting LiCl–KCl–CsCl eutectic at the temperature range 650–850 K on tungsten, gallium and cadmium electrodes in an inert gas atmosphere have been studied by non-stationary and stationary electrochemical methods. Reagents without contain impurities of moisture, oxygen and their compounds were used in the experiments. All major operations were performed in a dry glove box. The following methods were used to analyze the electrochemical processes: cyclic voltammetry, square-wave voltammetry and potentiometry at zero current. On cyclic voltammogram of the molten LiCl–KCl–CsCl–UCl3 solution on an inert tungsten electrode, one cathode current peak corresponding to the deposition of metallic uranium and one anode current peak associated with its dissolution were recorded. It was found that the potential of the cathode peak was shifted to a region of more negative values with an increase of the scan rate. The value of the cathode peak current was directly proportional vs. the square root of the polarization rate, but this dependence does not pass through the origin. Consequently, the system of U(III)/U(0) couple was irreversible and proceeds in one stage. It was found that on square-wave voltammograms in the studied “electrochemical window” the deposition of uranium on liquid reactive gallium and cadmium electrodes was carried out at more positive values than on inert tungsten electrode. It was established that this potential shift was associated with the formation of intermetallic compounds of uranium with the material of reactive electrodes. The values of the alloy formation potentials were determined. For identification of the composition of cathode deposits, potentiostatic electrolysis was performed. By X–ray diffraction analysis, it was found that the formation of the intermetallic compounds Ga3U and Ga2U occurs on the gallium reactive electrode, and Cd11U occurs on the cadmium one. The conditions of their formation during the electrolysis of molten LiCl–KCl–CsCl–UCl3 solutions were established. The reaction of the electrochemical extraction of uranium from molten LiCl–KCl–CsCl–UCl3 electrolyte was investigated on liquid reactive electrodes at different duration of electrolysis. It was found that the electrochemical extraction of uranium exceeds 97% on both Ga and Cd electrodes.

Electrochemical Mix-Reduction Process of U and U-Fe Alloys on the Surface of Cathode in LiCl-KCl-U3O8 at 773K

Electrochemical Behavior and Reduction of UO22+ in LiCl-KCl Molten Salt

Preparation of Γ-Uranium-molybdenum Alloys by Electrochemical Reduction of Solid Oxides in LiCl Molten Salt

Studies on the Electrodeposition of UO 2 Production in UO 2 Cl 2 -LiCl-KCl Melt

A Liquid Alloy Anode for the Electrolytic Reduction of Uranium Oxide in Molten Lithium Chloride

Fabrication of U-Ti alloy through direct electro-reduction from U3O8 and TiO2 mixtures in LiCl molten salt

ELECTROCHEMICAL SYNTHESIS OF INTERMETALLIC U–Ga AND U–Cd COMPOUNDS IN MOLTEN LiCl–KCl–CsCl EUTECTIC

The Electrode Kinetics of UCl3 in LiCl-KCl Molten Salt

Electrochemistry of Uranium on Liquid Cadmium Electrode in LiCl-KCl Eutectic

Capturing aqueous uranyl ions into catalytic nanometric shells of liquid metal droplets for electrochemical reduction

Impact of Ag on Electrochemical Recovery of UO 2 in Molten LiCl-KCl Salt

Electrochemical Drawdown of U 3+ and Ce 3+ in Molten LiCl-KCl Using a Liquid Cadmium Cathode

Chemical Species Transformation During the Dissolution Process of U3O8 and UO3 in the LiCl-KCl-AlCl3 Molten Salt

Chemical Species Transformation during the Dissolution Process of U 3 O 8 and UO 3 in the LiCl–KCl–AlCl 3 Molten Salt

Electrochemical Electron Transfer and Crystallization Process of Uranium (vi) in Sodium Salt Solution

Direct electrochemical reduction of low titanium chlorides into titanium aluminide alloy powders from molten eutectic KCl–LiCl–MgCl2

Cathode processes and uranium electrochemical extraction on W and Ga electrodes in LiCl–KCl melt

Fe-MMT/WO 3 composites for chemical and photocatalysis synergistic reduction of uranium (VI).

Electrochemical recovery of UO2 from LiCl-KCl-UO2F2 molten salt

Secondary metal ion-induced electrochemical reduction of U(VI) to U(IV) solids

Electrodeposition of aluminum on rare earth alloy surface in room temperature molten salts