Abstract:Provided a method to synthesize Nylon-6 oligomers with certain molecular weight and to further synthesize polyesteramides having short Nylon-6 segments connected by ester linkages. Polyamide prepolymer (PrePA) with molecular weight of 524. 6 to 808. 1 was synthesized by a ring-opening polymerization of epsilon-caprolactam in the presence of aminoethanol under the catalysis of H3PO3. The chain extension of the PrePAs was studied using N, N'-carbonylbiscaprolactamat (CBC) and 2, 2'-(1, 4-phenylene)-bis (2-oxazoline) (PBOX) as combined chain extenders. Through polycondensation of PrePA with adipic acid, polyesteramide prepolymers(PrePEA) with intrinsic viscosity of 0. 22 similar to 0. 30 dL/g were synthesized. Chain extension of the PrePEAs was carried out using PBOX and CBC as combined chain extenders and the chain extended polyesteramide (ExtPEA) with intrinsic viscosity up to 0. 74 dL/g was obtained. The ExtPEAs were characterized by FTIR and H-1-NMR spectra, differential scanning calorimetry (DSC), thermogravimetric analysis (TGA), wide angle X-ray scattering (WAXS) and tensile test. The DSC study showed that after chain extension the T-m and Delta H-m of the polyesteramides decreased. ExtPEA with [eta] of 0. 72 dL/g had the T-g of 30 degrees C and T-m of 163 degrees C. WAXS characterization showed that the ExtPEA had similar crystal characteristics to the Nylon-6 crystallites. TGA study showed that the ExtPEA had good thermal stability with initial decomposition temperature over 330 degrees C. Tensile test showed that typical ExtPEA samples had a tensile strength of 14. 1 MPa and a strain at break of 68. 6%. The ExtPEA has high Tm, good thermal stability and moderate tensile strength, and is suitable for melt processing. Meanwhile, presence of the ester linkages and lower crystallinity in the ExtPEA may lead to improved biodegradability of the ExtPEA compared to the normal nylon-6.

Studies on the Synthesis and Properties of Aliphatic Thermoplastic Polyurethanes via Non-isocyanate Route

Synthesis and Characterization of Aliphatic Poly(Amide Urethane)S Having Different Nylon 6 Segments Through Non-Isocyanate Route

High Molecular Weight Polyesters Derived from Biobased 1,5-Pentanediol and a Variety of Aliphatic Diacids: Synthesis, Characterization, and Thermo-Mechanical Properties

Oriented distribution structure, interaction, and performance of thermoplastic polyurethane/selective hindered amine hybrids

Synthesis and Characterization of Crystallizable Aliphatic Thermoplastic Poly(ester Urethane) Elastomers Through a Non-Isocyanate Route

Aliphatic Thermoplastic Poly(Ether Urethane)S Having Long Peg Sequences Synthesized Through A Non-Isocyanate Route

Crystallizable and Tough Aliphatic Thermoplastic Polyureas Synthesized Through a Nonisocyanate Route

Aliphatic Thermoplastic Polyurethane-Ureas and Polyureas Synthesized Through a Non-Isocyanate Route

Synthesis and Properties of Non-Isocyanate Thermoplastic Polyurethanes Containing Dibutylene Terephthalate Units

Synthesis, Characterization and Non-Isothermal Crystallization Kinetics of a New Family of Poly (Ether-Block-Amide)s Based on Nylon 10T/10I

Non-Isocyanate Aliphatic-Aromatic Poly(carbonate-urethane)s-An Insight into Transurethanization Reactions and Structure-Property Relationships

Mechanical properties of thermoplastic polyurethanes containing aliphatic polycarbonate soft segments with different chemical structures

Synthesis and characterization of polyesteramides having short Nylon-6 segments in the main chains through polycondensation and chain extension

Synthesis and properties of high performance thermoplastic polycarbonate polyurethane elastomers through a non-isocyanate route

Study on Synthesis and Properties of Novel HTPB/PEG Polyurethane Copolymers

Preparation of Polyurethane‐Urea Elastomers Using Low Molecular Weight Aliphatic Diamines Enabled by Reversible CO2 Chemistry

Synthesis and Characterization of Biodegradable Polyurethanes with Unsaturated Carbon Bonds Based on Poly(Propylene Fumarate)

Synthesis and Properties of Polyesteramides Having Short Nylon-610 Segments in the Main Chains Through Polycondensation and Chain Extension

A Non-Isocyanate Route to Poly(Ether Urethane): Synthesis and Effect of Chemical Structures of Hard Segment

Preparation and Characterization of a Series of Polyamides with Long Alkylene Segments: Nylons 12 20, 10 20,s 20,6 20, 4 20 and 2 20

SYNTHESIS AND CHARACTERIZATION OF POLYESTERAMIDES DERIVED FROM Ε-Caprolactam AND AMINOETHANOL