Abstract:The C=C double bonds in the main chain of hydroxyl-terminated polybutadiene (DHTPB), obtained by the degradation of polybutadiene rubber, were partially epoxided using m-chloroperoxybenzoic acid (mCPBA) as epoxidation reagent. A series of epoxided HTPBs (EHTPB) with different epoxy contents (5%, 10% and 15%) were prepared by tuning the molar ratio of mCPBA to C=C double bonds. The structures of EHTPBs were characterized by Fourier transform-infrared (FTIR), nuclear magnetic resonance (H-1-NMR) spectroscopy and gel permeation chromatography (GPC). The epoxy percent in EHTPBs from H-1-NMR spectra was in accordance with the design. In addition, a series of EHTPB-based polyurethane elastomers (EPU) were prepared by the reaction between EHTPB and 4,4'-diphenylmethane diisocyanate with 1,4-butanediol as a chain extender. Mechanical and thermal properties of the EPU samples were characterized by tensile test, differential scanning calorimetry (DSC) and thermal gravity analysis (TGA). With increased epoxy percent in EHTPB, the Young's modulus and the tensile strength of the EPU samples increased, whereas the elongation at break decreased. The sample EPU10 prepared with 10% of epoxy had the best mechanical properties with 8.82 MPa as Young's modulus, 7.83 MPa as tensile strength, and (485 +/- 23)% as elongation at break. The elasticity recovery of the EPU sample was slightly better than HTPB-based PU (EPU0). The results with TGA test showed that the thermal degradation of EPU, similar to EPU0, was divided into three stages. However, the EPU samples had better thermal stability with the initial degradation temperature at 210 degrees C, about 30 degrees C higher than that of EPU0. The DSC results showed that the glass transition temperature (T-g) of EPU gradually increased as epoxy percent was increased, though still lower than that of HTPB (FHTPB) based PUs prepared by free-radical polymerization.

Synthesis and Properties of Non-Isocyanate Thermoplastic Polyurethanes Containing Dibutylene Terephthalate Units

Facile Synthesis of Novel HTPBs and EHTPBs with High Cis-1,4 Content and Extremely Low Glass Transition Temperature

Preparation and Properties of Epoxided Hydroxyl-terminated Polybutadiene Based Polyurethane Elastomers

High Cis-1,4 Hydroxyl-Terminated Polybutadiene-Based Polyurethanes with Extremely Low Glass Transition Temperature and Excellent Mechanical Properties

Modification of Unsaturated Polyester Resin by HTPB: Effect of Introducing Method of the Rubber

Oriented distribution structure, interaction, and performance of thermoplastic polyurethane/selective hindered amine hybrids

The Structure and Dynamic Properties of Thermoplastic Polyurethane Elastomer/Hindered Phenol Hybrids

Synthesis and Characterization of Crystallizable Aliphatic Thermoplastic Poly(ester Urethane) Elastomers Through a Non-Isocyanate Route

Synthesis of Hydroxyl-Terminated Polybutadiene Possessing High Content of 1,4-Units Via Anionic Polymerization

Studies on the Synthesis and Properties of Aliphatic Thermoplastic Polyurethanes via Non-isocyanate Route

Crystallizable and Tough Aliphatic Thermoplastic Polyureas Synthesized Through a Nonisocyanate Route

Aliphatic Thermoplastic Poly(Ether Urethane)S Having Long Peg Sequences Synthesized Through A Non-Isocyanate Route

Synthesis of Thermoplastic Polyurethanes Containing Bio-Based Polyester Polyol and Their Fiber Property

Thermoplastic polyurethane with good mechanical and processing performances via blocking and deblocking of isocyanates

One-Shot Synthesis of Thermoplastic Polyurethane Based on Bio-Polyol (Polytrimethylene Ether Glycol) and Characterization of Micro-Phase Separation

Morphology and properties of high molecular weight polyisobutylene and thermoplastic polyurethane elastomer

Macromolecular metamorphosis of thermoplastic poly(thio)urethanes containing boronic acid esters

Study on Properties and Preparation of Thermoplastic Polyurethane Hot-Melt Adhesive

Synthesis of non‐isocyanate polyurethanes with high‐performance and self‐healing properties

Solvent-Free One-Shot Synthesis of Thermoplastic Polyurethane Based on Bio-Poly(1,3-propylene succinate) Glycol with Temperature-Sensitive Shape Memory Behavior

Tuning the Properties of Bio-based Thermoplastic Polyurethane Derived from Polylactic Acid by Varying Chain Extenders and Hard Segment Contents