Abstract:The C=C double bonds in the main chain of hydroxyl-terminated polybutadiene (DHTPB), obtained by the degradation of polybutadiene rubber, were partially epoxided using m-chloroperoxybenzoic acid (mCPBA) as epoxidation reagent. A series of epoxided HTPBs (EHTPB) with different epoxy contents (5%, 10% and 15%) were prepared by tuning the molar ratio of mCPBA to C=C double bonds. The structures of EHTPBs were characterized by Fourier transform-infrared (FTIR), nuclear magnetic resonance (H-1-NMR) spectroscopy and gel permeation chromatography (GPC). The epoxy percent in EHTPBs from H-1-NMR spectra was in accordance with the design. In addition, a series of EHTPB-based polyurethane elastomers (EPU) were prepared by the reaction between EHTPB and 4,4'-diphenylmethane diisocyanate with 1,4-butanediol as a chain extender. Mechanical and thermal properties of the EPU samples were characterized by tensile test, differential scanning calorimetry (DSC) and thermal gravity analysis (TGA). With increased epoxy percent in EHTPB, the Young's modulus and the tensile strength of the EPU samples increased, whereas the elongation at break decreased. The sample EPU10 prepared with 10% of epoxy had the best mechanical properties with 8.82 MPa as Young's modulus, 7.83 MPa as tensile strength, and (485 +/- 23)% as elongation at break. The elasticity recovery of the EPU sample was slightly better than HTPB-based PU (EPU0). The results with TGA test showed that the thermal degradation of EPU, similar to EPU0, was divided into three stages. However, the EPU samples had better thermal stability with the initial degradation temperature at 210 degrees C, about 30 degrees C higher than that of EPU0. The DSC results showed that the glass transition temperature (T-g) of EPU gradually increased as epoxy percent was increased, though still lower than that of HTPB (FHTPB) based PUs prepared by free-radical polymerization.

Aliphatic Thermoplastic Poly(Ether Urethane)S Having Long Peg Sequences Synthesized Through A Non-Isocyanate Route

High-Performance Olefin Thermoplastic Elastomer Based on Dynamically Cross-Linking Crystalline Macromers and Elastic Backbones

Preparation and Properties of Epoxided Hydroxyl-terminated Polybutadiene Based Polyurethane Elastomers

Synthesis and Characterization of Crystallizable Aliphatic Thermoplastic Poly(ester Urethane) Elastomers Through a Non-Isocyanate Route

Synthesis and Properties of Non-Isocyanate Aliphatic Thermoplastic Polyurethane Elastomers with Polycaprolactone Soft Segments

Synthesis and properties of biobased non-isocyanate aliphatic thermoplastic polyurethane elastomers with butanediurethane hard segments

Crystallizable and Tough Aliphatic Thermoplastic Polyureas Synthesized Through a Nonisocyanate Route

Studies on the Synthesis and Properties of Aliphatic Thermoplastic Polyurethanes via Non-isocyanate Route

Synthesis and properties of high performance thermoplastic polycarbonate polyurethane elastomers through a non-isocyanate route

Synthesis and Characterization of Aliphatic Poly(Amide Urethane)S Having Different Nylon 6 Segments Through Non-Isocyanate Route

Aliphatic Thermoplastic Polyurethane-Ureas and Polyureas Synthesized Through a Non-Isocyanate Route

Poly(ethylene 2,5-Furandicarboxylate-mb-poly(tetramethylene Glycol)) Multiblock Copolymers: from High Tough Thermoplastics to Elastomers

Synthesis and Properties of Non-Isocyanate Thermoplastic Polyurethanes Containing Dibutylene Terephthalate Units

Synthesis and Characterization of Thermoplastic Polyether-imide Elastormer

A new class of poly(ether‐ block ‐amide)s based on semi‐aromatic polyamide: synthesis, characterization and structure–property relations

Synthesis and Characterization of Inherently Flame‐retardant and Anti‐dripping Thermoplastic Poly(imides‐urethane)s

Synthesis And Properties Of Poly(Ester Urethane)S Consisting Of Poly(L-Lactic Acid) And Poly(Ethylene Succinate) Segments

Synthesis and Flame Retardancy of Novel Thermally Stable Poly(imideurethane)s Containing Imide and Alkynyl Groups in Main Chain

Morphology and Properties of Novel Thermoplastic Polyurethane Elastomer

Synthesis and characterization of new thermoplastic poly(ester-ether-imide) elastomers derived from N',N-bis(2-hydroxyethyl)-pyromellitimide unit with excellent thermal stability and good fiber-forming property

Synthesis and characterization of thermally stable poly(urethane-imide)s based on novel diols-containing imide and alkynyl groups