Abstract:The C=C double bonds in the main chain of hydroxyl-terminated polybutadiene (DHTPB), obtained by the degradation of polybutadiene rubber, were partially epoxided using m-chloroperoxybenzoic acid (mCPBA) as epoxidation reagent. A series of epoxided HTPBs (EHTPB) with different epoxy contents (5%, 10% and 15%) were prepared by tuning the molar ratio of mCPBA to C=C double bonds. The structures of EHTPBs were characterized by Fourier transform-infrared (FTIR), nuclear magnetic resonance (H-1-NMR) spectroscopy and gel permeation chromatography (GPC). The epoxy percent in EHTPBs from H-1-NMR spectra was in accordance with the design. In addition, a series of EHTPB-based polyurethane elastomers (EPU) were prepared by the reaction between EHTPB and 4,4'-diphenylmethane diisocyanate with 1,4-butanediol as a chain extender. Mechanical and thermal properties of the EPU samples were characterized by tensile test, differential scanning calorimetry (DSC) and thermal gravity analysis (TGA). With increased epoxy percent in EHTPB, the Young's modulus and the tensile strength of the EPU samples increased, whereas the elongation at break decreased. The sample EPU10 prepared with 10% of epoxy had the best mechanical properties with 8.82 MPa as Young's modulus, 7.83 MPa as tensile strength, and (485 +/- 23)% as elongation at break. The elasticity recovery of the EPU sample was slightly better than HTPB-based PU (EPU0). The results with TGA test showed that the thermal degradation of EPU, similar to EPU0, was divided into three stages. However, the EPU samples had better thermal stability with the initial degradation temperature at 210 degrees C, about 30 degrees C higher than that of EPU0. The DSC results showed that the glass transition temperature (T-g) of EPU gradually increased as epoxy percent was increased, though still lower than that of HTPB (FHTPB) based PUs prepared by free-radical polymerization.

Mechanical properties of thermoplastic polyurethanes containing aliphatic polycarbonate soft segments with different chemical structures

Preparation and Properties of Epoxided Hydroxyl-terminated Polybutadiene Based Polyurethane Elastomers

The Structure and Dynamic Properties of Thermoplastic Polyurethane Elastomer/Hindered Phenol Hybrids

Oriented distribution structure, interaction, and performance of thermoplastic polyurethane/selective hindered amine hybrids

Effect of soft segment structure on properties of polyurethane elastomers

Polycarbonate-based thermoplastic polyurethane elastomers modified by DMPA

The relationship between chemical microstructure, crystallinity, mechanical properties, and CO2/N2 gases permselectivity of thermoplastic polyurethane membranes

Effect of the cyclic structure content on aliphatic polycarbonate-based polyurethane

Effect of Chain Extender on Hydrogen Bond and Microphase Structure of Biodegradable Thermoplastic Polyurethanes

Copolymerization approach of soft segment towards the adhesion improvement of polycarbonate-based thermoplastic polyurethane

Study on mechanical, thermal and shape memory properties of polycarbonate/thermoplastic polyurethane blends

Synthesis and properties of high performance thermoplastic polycarbonate polyurethane elastomers through a non-isocyanate route

Enhanced polyurethanes based on different polycarbonatediols

Thermoplastic polyurethane-based polycarbonate diol hot melt adhesives: The effect of hard-soft segment ratio on adhesion properties

Tuning the Properties of Bio-based Thermoplastic Polyurethane Derived from Polylactic Acid by Varying Chain Extenders and Hard Segment Contents

Study on Properties and Preparation of Thermoplastic Polyurethane Hot-Melt Adhesive

Investigating the Effect of Chain Extender on the Phase Separation and Mechanical Properties of Polybutadiene-Based Polyurethane

Block length distribution, morphology, and property of thermoplastic polyurethanes affected by production method: A polymer‐by‐process investigation

Studies on the Synthesis and Properties of Aliphatic Thermoplastic Polyurethanes via Non-isocyanate Route

Structural and Viscoelastic Properties of Thermoplastic Polyurethanes Containing Mixed Soft Segments with Potential Application as Pressure Sensitive Adhesives

Regulating the structure of thermoplastic polyurethane elastomers with a diol chain extender to strength performance