Abstract:Scanning probe microscopy was used to simultaneously determine the molecular chain structure and intrinsic mechanical properties, including anisotropic elastic modulus and friction, for lamellae of highly oriented high-density polyethylene (HDPE) obtained by the melt-drawn method. The molecular-scale image of the highly oriented lamellae by friction force microscopy (FFM) clearly shows that the molecular chains are aligned parallel to the drawing direction, and the periodicities along and perpendicular to the drawing direction are 0.26 and 0.50 nm, respectively. The results indicate that the exposed planes of the lamellae resulting from the melt-drawn method are (200), which is consistent with results of transmission electron microscopy and electron diffraction. Because of the high degree of anisotropy in the sample, coming from alignment of the molecular chains along the drawing direction, the measured friction force, F, determined by FFM is strongly dependent on the angle, theta, between the scanning direction and the chain axis. The force increases as theta is increased from 0 degrees (i.e., parallel to the chain axis) to 90 degrees (i.e., perpendicular to the chain axis). The structural anisotropy was also found to strongly influence the measurements of the transverse chain modulus of the polymer by the nanoindentation technique. The measured value of 13.8 GPa with transverse modulus was larger than the value 4.3 GPa determined by wide-angle X-ray diffraction, which we attributed to anisotropic deformation of the lamellae during nanoindentation measurements that was not accounted for by the elastic treatment we adopted from Oliver and Pharr. The present approach using scanning probe microscopy has the advantage that direct correlations between the nanostructure, nanotribology, and nanomechanical properties of oriented samples can be determined simultaneously and simply.

Local measurements of stored energy: Microstructural and stereological considerations

Microstructural-Based Measurement of Local Stored Energy Variations in Deformed Metals

Measurement of Orientation Dependent Stored Energy of Deformation on A Local Scale

Stored Energy, Microstructure, and Flow Stress of Deformed Metals

Modeling Energy Storage and Structural Evolution During Finite Viscoplastic Deformation of Glassy Polymers

Nanostructure and Mechanical Measurement of Highly Oriented Lamellae of Melt-Drawn HDPE by Scanning Probe Microscopy

Stored Energy and Structure in Top-Down Processed Nanostructured Metals

Stored Energy in Nickel Cold Rolled to Large Strains, Measured by Calorimetry and Evaluated from the Microstructure

Statistical TEM analysis of boundary misorientations in aluminium deformed to large and extra large strains by ECAE

Length scale effects on deformation microstructure formation in the near micrometre grain size regime

Microstructure and Stress Mapping in 3D at Industrially Relevant Degrees of Plastic Deformation

A Simplified Deformation Gradient Theory and Its Experimental Verification

Accounting for localized deformation: a simple computation of true stress in micropillar compression experiments

Analysis of Stored Energy in Cold-Rolled Copper Using Bulk and Microstructure-Based Techniques

Characterization and Influence of Deformation Microstructure Heterogeneity on Recrystallization

In-situ Study of Microstructural Evolution and Local Strain Distribution During Tensile Loading of Near-Micrometre Grain Size Aluminium

Investigation of Medium to High Strain Deformation Microstructures Using an Automated Electron Backscattering Pattern (EBSP) System

3D Microstructural and Strain Evolution During the Early Stages of Tensile Deformation

Micromechanical measurements of local plastic events in granular materials

Heterogeneous local plastic deformation of interstitial free steel revealed using in-situ tensile testing and high angular resolution electron backscatter diffraction

Deformation analysis in microstructures and micro-devices