Abstract:A simple, room-temperature bonding process was developed for the fabrication of glass microfluidic chips. High-quality bonding with high yields (>95%) was achieved without the requirement of clean room facilities, programmed high-temperature furnaces, pressurized water sources, adhesives, or pressurizing weights. The plates to be bonded were sequentially prewashed with acetone, detergent, high-flow-rate (10-20 m/s) tap water, and absolute ethyl alcohol and were soaked in concentrated sulfuric acid for 8-12 h. The plates were again washed in high-flow-rate tap water for 5 min and, finally, with demineralized water. The plates were bonded by bringing the cleaned surfaces into close contact under a continuous flow of demineralized water and air-dried at room temperature for more than 3 h. This bonding process features simple operation, good smoothness of the plate surface, and high bonding yield. The procedures can be readily applied in any routine laboratory. The bonding strength of glass chips thus produced, measured using a shear force testing procedure, was higher than 6 kg/cm(2). The mechanism for the strong bonding strength is presumably related to the formation of a hydrolyzed layer on the plate surfaces after soaking the substrates in acid or water for extended periods. Microfluidic chips bonded by the above procedure were tested in the CE separation of fluorescein isothiocyanate-labeled amino acids.

A room-temperature bonding of glass nanofluidic chips utilizing a surface activation with a fluorine-containing plasma treatment

Bonding of Glass-Based Microfluidic Chips at Low- or Room-Temperature in Routine Laboratory

A Simple Low-Temperature Glass Bonding Process with Surface Activation by Oxygen Plasma for Micro/Nanofluidic Devices

Bonding of Glass Microfluidic Chips at Room Temperatures

Micro Fabrication of Micro Fluidic Glass Chip Without Clean Room Condition

Research on Silicon-Glass Direct Bonding at Room Temperature

Fabrication of Fluidic Chips with 1-D Nanochannels on PMMA Substrates by Photoresist-Free UV-lithography and UV-assisted Low-Temperature Bonding

High-refractive-index glass device fabricated by room temperature bonding

Fabrication of 1-d nanochannels on PMMA substrate by photoresist-free uv lithography and UV-assisted bonding under low temperature

Low‐temperature bonding of glasses: The role of plasma‐engrafted surface amino groups

Fabrication and Characterization of 20 Nm Planar Nanofluidic Channels by Glass-Glass and Glass-Silicon Bonding

Low-deformation precision thermal bonding of nanostructured microfluidic chips

Fabrication of full glass chips with hybrid micro- and nanochannels and their application to protein concentration

Fabrication of Micro/Nanofluidic Chip on Glass Substrate and Its Application for Electrokinetic Concentration of Proteins

Fabrication of 1D nanofluidic channels on glass substrate by wet etching and room-temperature bonding

A 64-Pin Nanowire Surface Fastener Like a Ball Grid Array Applied for Room-temperature Electrical Bonding

Diffusion Bonding of a Zr-based Metallic Glass in Its Supercooled Liquid Region

Mechanisms for room temperature direct wafer bonding

Nanoporous Structure Fabrication on Glass Surfaces for Enhanced Glass Adhesion Using Hydrogen Fluoride Gas

Mechanical and electrical cold bonding based on metallic nanowire surface fasteners.

A simple approach to fabricate multi-layer glass microfluidic chips based on laser processing and thermocompression bonding