Studies of Tio . 5 ZrO . S 02 supported CuO catalysts for NO + CO reaction *

Guang-hui Dingl,Xiao-yuan Jiangl,Yue-juan Wang,Xiao-ming Zheng

2012-01-01

Abstract:The activi ties of CuO supported on Tio.sZro.s0 2 have been exam ined with a microreactor-GC NO+CO reaction system and the catalysts characterized by BET, TPR, TG-OTA, XRO and NO-TPO. Experimental results show that the CuOffio sZro.50Z activities increase wi th increase in CuO loading. To obtain 99% NO conversion, the reaction temperature needed to be 350°C in air but on ly 200°C in Hz atmosphere. TPR analysis shows two peaks (a and p peaks) lit CuO loading of:::: 12%, while a third peak (y peak) occurs with higher CuO load ing at 300°C. The a peak is attributed to highly di spersed CuO, the p peak to isolated CuO and the y peak to crystal CuO. TG-OTA also shows endothermic peak at low temperature (120°C) and exothermic peak at high temperature (725°C), indicat ing the completion of ZrTi04 crystallization. From the XRD analysis, it has been found that there is no CuO crystal diffraction peaks at 12% CuO loadi ng, but two CuO crystal diffraction peaks at 2035.5° and 38.7° are present at 18% CuO loading. With increase in CuO loading, the intensity o f CuO diffraction peaks is increased. In addition , NO-TPD analysis shows that NO adsorption and desorption by TiosZro.s02 in air are s imil ar to those in Hz atmosphere. In air atmosphere, both CuOffio.5Zro.502 and Tio.5Zro.50Z have two adsorption peaks, but the former has lower desorption peak temperature than the latter, suggesting that the activity of NO decomposition by CuOffio.5Zro.50 2 is hi gher than that by Tio.sZro.s02. In Hz atmosphere, the high temperature desorption peak d isappears and there onl y exists one low temperature desorption peak at 150°C, inferring that the high temperature adsorption site is probably Cu2+ and the low temperature adsorption s ite is CUD. IPC Code: InL CL BOlJ 21106